| Résumé : |
Chemical changes, measured using spectroscopy, and crosslink density, measured by mechanical thermal analysis, were determined during accelerated weathering on a model polyester-urethane coating of known composition. The tensile modulus, measured above the glass transition temperature, and thus the crosslink density, decreased with exposure, as expected from the chemical changes. However, the tensile modulus, measured at room temperature, increased with exposure. Physical aging of the polymer network was found to occur concurrently with photodegradation and accounts for much of the increase in room temperature modulus. Increased hydrogen bonding in the increasingly oxidized polyester-urethane may also contribute to the increase in modulus at room temperature. Both physical and chemical changes must be determined if changes, and rates of change, in performance due to weathering are to be understood. |
Aller sur edunet
Accueil
Mechanical property changes and degradation during accelerated weathering of polyester-urethane coatings in JOURNAL OF COATINGS TECHNOLOGY AND RESEARCH, Vol. 3, N° 1 (01/2006)