In order to study the effects of coal tar components on the adhesion strength of a heavy duty anticorrosive coating formed with tar-urethane resin on a steel plate, polyurethane coatings that were compounded with 15 kinds of polycyclic aromatic compounds as model coal tar components were prepared. In the model coal tar components, naphthalene, quinoline, 2-naphthol, and phenanthrene showed good compatibility with polyurethane. To test their heavy duty anticorrosive properties, tensile adhesion strength of the cured coatings prepared with the compatible model coal tar components was measured, and the change in tensile adhesion strength as a function of time during salt-water spray treatment was measured. We found that the systems compounded with naphthalene, 2-naphthol, and phenanthrene showed good properties in an ordinary state for adhesion strength. However, only the system with 2-naphthol was found to have good properties in the change of tensile adhesion strength as a function of time during salt-water spray treatment. The curing time of the system with 2-naphthol was slower than that of the others, i.e., we found an inverse proportion between curing speed and adhesion durability. We also measured the dynamic viscoelasticity of cured coatings. We found that a tan delta curve of the system with 2-naphthol shifted towards a low temperature side and the tan delta at the temperature at which adhesion strength was measured was larger than that of the others. We hypothesized that the reason for the tan delta shift was a result of the decrease in crosslinking density because 2-naphthol partially capped the isocyanate group. Considering these results, we hypothesized that one of the reasons why the adhesion properties of the system with 2-naphthol had improved was due to the increase of tan delta. |
Aller sur edunet
Accueil
Ajouter le résultat dans votre panier Affiner la rechercheEffects of model coal tar components on adhesion strength of polyurethane coating on steel plate / Naoki Yokoyama in JOURNAL OF COATINGS TECHNOLOGY AND RESEARCH, Vol. 2, N° 6 (04/2005)