[article]
| Titre : |
Nano-mechanical properties and topography of thermosetting acrylic powder coatings |
| Type de document : |
texte imprimé |
| Auteurs : |
D. C. Andrei, Auteur ; D. Parsonage, Auteur ; B. J. Briscoe, Auteur ; S. G. Yeates, Auteur ; J. N. Hay, Auteur ; Joseph L. Keddie, Auteur |
| Année de publication : |
2001 |
| Article en page(s) : |
p. 65-73 |
| Note générale : |
Bibliogr. |
| Langues : |
Américain (ame) |
| Tags : |
Matériau revêtement Peinture poudre Propriété mécanique Feuil Structure surface Thermodurcissable Acrylique dérivé polymère Résistance rayure Vernis Dureté Microdureté Module élasticité Topographie Etude expérimentale |
| Index. décimale : |
667.9 Revêtements et enduits |
| Résumé : |
Both nano-scratching and nano-indentation techniques have been used to evaluated the mechanical properties of the surface of acrylic coatings, with and without added pigment. The coatings were formed from thermosetting, acrylic powders. Both types of coatings-clear and pigmented-do not exhibit any significant differences in their hardness with an increase in baking time from 7 to 15 min. According to the scratching profiles, the deformation induced at the surface is virtually elastic. Introducing the pigment causes a slight increase in the elastic modulus but not significant variation in hardness. In all coatings, the computed hardness and the elastic modulus vaues are higher near the surface (perhaps as a result of tip geometry effects), but these readily reach plateau values that are consistent with other work available in the literature. A long-range surface profiler, which provided two-dimensional and three-dimensional topographical maps of the coatings surfaces, reveals undulations in the surface with a wavelength on the order of 2-4 mm. Moreover, the topography of the pigmented coating is significantly smoother than that of the clear coating in which shallow pits (about 100 µm in diameter) are randomly distributed at the surface. The nano-mechanical properties within these pits are similar to the bulk of the coating. |
| Permalink : |
https://e-campus.itech.fr/pmb/opac_css/index.php?lvl=notice_display&id=5688 |
in JOURNAL OF COATINGS TECHNOLOGY (JCT) > Vol. 73, N° 912 (01/2001) . - p. 65-73
[article]
|
Aller sur edunet
Accueil
Nano-mechanical properties and topography of thermosetting acrylic powder coatings in JOURNAL OF COATINGS TECHNOLOGY (JCT), Vol. 73, N° 912 (01/2001)