Abrasion resistance of polymer and polymer–ceramic composite coatings for steel hydraulic structures |
| Type de document : |
texte imprimé |
| Auteurs : |
P. V. Vijay, Auteur ; Piyush R. Soti, Auteur ; Derrick A. Banerjee, Auteur ; Konstantinos A. Sierros, Auteur |
| Année de publication : |
2020 |
| Article en page(s) : |
p. 401-411 |
| Note générale : |
Bibliogr. |
| Langues : |
Américain (ame) |
| Catégories : |
Anticorrosion
Essais de résilience
Matériaux céramiques
Mouillabilité
Mouillage (chimie des surfaces)
Polyéthylène haute densité
Profilométrie
Résistance à l'abrasion
Résistance à l'usure
Revêtements organiques
|
| Index. décimale : |
667.9 Revêtements et enduits |
| Résumé : |
There is an increased demand for abrasive wear-resistant coatings that add durability to steel hydraulic structures, particularly for those subjected to flowing water with debris and alternate wet/dry cycles. These coating systems provide not only corrosion and chemical resistance, but also good erosion and abrasion resistance to the metallic surfaces, which are constantly exposed to flowing water containing sand particles and debris. Generally, vinyl-based coatings are used on hydraulic steel structures to protect them from corrosion and abrasion. However, due to the existence of high water force and debris, the coating is abraded at a faster rate leading to significant maintenance and repair costs. In this study, abrasive wear resistance of conventional vinyl-based coating systems currently used on lock and dam steel structures by U.S. Army Corps of Engineers has been compared with polymer matrix composite coatings, fibrous polymer coatings, and ultrahigh molecular weight polyethylene (UHMWPE). Six coating systems were evaluated through two-body abrasion tests using a reciprocating abrader under dry and wet conditions. Furthermore, wettability of the coating systems and its effect on the wear rate under the presence of water was studied. In addition, scanning electron microscopy of the wear tracks on different coatings was conducted to study and identify their failure mechanisms. Based on the results, UHMWPE and polymer–ceramic composite coatings were found to perform significantly better than the conventional vinyl-based coatings. |
| Note de contenu : |
- EXPERIMENTAL DETAILS : Coating systems - Surface preparation for application of coatings - Wear tests - Surface wettability
- RESULTS AND DISCUSSION : Depth and volume of coating abrasion - Rate of abrasive wear - Effect of surface wettability - Wear mechanisms and failure of coatings - Field implementation and inspection of coatings |
| DOI : |
https://doi.org/10.1007/s11998-019-00286-3 |
| En ligne : |
https://link.springer.com/content/pdf/10.1007/s11998-019-00286-3.pdf |
| Format de la ressource électronique : |
Pdf |
| Permalink : |
https://e-campus.itech.fr/pmb/opac_css/index.php?lvl=notice_display&id=33991 |
in JOURNAL OF COATINGS TECHNOLOGY AND RESEARCH > Vol. 17, N° 2 (03/2020) . - p. 401-411
Aller sur edunet
Accueil
Ajouter le résultat dans votre panier Affiner la rechercheA350 XWB composite bonded repair in JEC COMPOSITES MAGAZINE, N° 128 (05-06/2019)
Adhésifs. Essai de tenue au choc par cisaillement du joint adhésif - Norme NF EN ISO 9653 / Saint-Denis La Plaine : Association Française de Normalisation (AFNOR) (2001)