Synthesis of core–shell-type styrene acrylic latexes with low NMA content and their application in pigment printing pastes / Mesut Eren in JOURNAL OF COATINGS TECHNOLOGY AND RESEARCH, Vol. 15, N° 1 (01/2018)
[article]
Titre : Synthesis of core–shell-type styrene acrylic latexes with low NMA content and their application in pigment printing pastes Type de document : texte imprimé Auteurs : Mesut Eren, Auteur ; Gökhan Akbulut, Auteur ; Sanem Senler ; Burcak Karaguzel Kayaoglu Année de publication : 2018 Article en page(s) : p. 121–129 Note générale : Bibliogr. Langues : Américain (ame) Catégories : Analyse thermique
Copolymère styrène acrylique
Copolymères -- Synthèse
Core-Shell
CotonLe coton est une fibre végétale qui entoure les graines des cotonniers "véritables"(Gossypium sp.), un arbuste de la famille des Malvacées. Cette fibre est généralement transformée en fil qui est tissé pour fabriquer des tissus. Le coton est la plus importante des fibres naturelles produites dans le monde. Depuis le XIXe siècle, il constitue, grâce aux progrès de l'industrialisation et de l'agronomie, la première fibre textile du monde (près de la moitié de la consommation mondiale de fibres textiles).
Fibres polyesters
Formaldéhyde
Impression sur étoffes
Latex
Liants
Pigments
Réduction des composés organiques volatils
Résistance à l'abrasion
Résistance au lavage
Résistance aux frottements humides
Taille des particulesIndex. décimale : 667.9 Revêtements et enduits Résumé : In this paper, novel core–shell polymers comprising styrene (St) and butyl acrylate (BA) in both core and shell layers of the polymer particles have been synthesized and employed in pigment printing pastes which were applied on 100% cotton and 65% cotton/35% polyester (PET) fabrics. The aim was to reduce the NMA content and the formation of free formaldehyde from pigment printing pastes by employing newly synthesized core-/shell-type polymers. After five washing cycles, the synthesized core-/shell-type polymer including 1% NMA in the core and 1% NMA in the shell with T g values +30°C and −20°C, respectively, with lowest total NMA content (1.03%) yielded the best result and showed closest ΔE values to the commercially available polymer including 4% NMA. Dry and wet rubbing fastness results showed no significant changes in the absence of NMA when compared with NMA containing samples. The penetration degree of the pigment pastes of the corresponding polymers was relatively higher on 100% cotton fabric for both red- and blue-colored pigments. A negligible decrease in color strength has been observed for all polymers when colored in red. Note de contenu : - EXPERIMENTAL : Materials - Core/shell latex synthesis - Preparation of the pigment printing pastes - Characterization - Application of pigment printing pastes - Testing of printed fabrics
- RESULTS AND DISCUSSION : Characterization of the core/shell latexes - DSC analysis - Particle size of the core/shell binder - The performance of core/shell binders in pigment printing pastes - Dry and wet rubbing fastness and hand feeling of the printed fabrics - Color strength and penetration - Washing fastnessDOI : 10.1007/s11998-017-9955-0 En ligne : https://link.springer.com/content/pdf/10.1007%2Fs11998-017-9955-0.pdf Format de la ressource électronique : Permalink : https://e-campus.itech.fr/pmb/opac_css/index.php?lvl=notice_display&id=30091
in JOURNAL OF COATINGS TECHNOLOGY AND RESEARCH > Vol. 15, N° 1 (01/2018) . - p. 121–129[article]Réservation
Réserver ce document
Exemplaires (1)
Code-barres Cote Support Localisation Section Disponibilité 19610 - Périodique Bibliothèque principale Documentaires Disponible