Hydroxyapatite nanoparticles and polyethylene glycol treatment of historical leather : mechanical properties / Amir Ershad-Langroudi in JOURNAL OF THE AMERICAN LEATHER CHEMISTS ASSOCIATION (JALCA), Vol. CVIII, N° 12 (12/2013)  

[article]  inJOURNAL OF THE AMERICAN LEATHER CHEMISTS ASSOCIATION (JALCA) > Vol. CVIII, N° 12 (12/2013) Titre : Hydroxyapatite nanoparticles and polyethylene glycol treatment of historical leather : mechanical properties Type de document : texte imprimé Auteurs : Amir Ershad-Langroudi, Auteur ; Akram Mirmontahai, Auteur Année de publication : 2013 Note générale : Bibliogr. Langues : Américain (ame) Catégories : Analyse thermomécanique dynamique Cuirs et peaux -- Propriétés mécaniques Essais accélérés (technologie) Essais dynamiques Hydroxyapatite L'hydroxyapatite est une espèce minérale de la famille des phosphates, de formule Ca5(PO4)3(OH), usuellement écrite Ca10(PO4)6(OH)2 pour souligner le fait que la maille de la structure cristalline comprend deux molécules. L'hydroxyapatite est le membre hydroxylé du groupe apatite. L'ion OH- peut être remplacé par le fluor, le chlore ou le carbonate. L'hydroxyapatite cristallise dans le système hexagonal. La poudre d'hydroxyapatite pure est blanche. Celles que l'on trouve dans la nature peuvent cependant être de couleur marron, jaune ou verte. Microscopie électronique à balayage Microscopie électronique en transmission Nanoparticules Polyéthylène glycol Traction (mécanique) Index. décimale : 675 Technologie du cuir et de la fourrure Résumé : Historical leather objects are at risk of deterioration through mechanical stress such as viscoelastic and plastic deformation as well as natural aging erosion. So, it was expected that appropriate leather treatment should improve their mechanical properties. For this purpose, the mechanical behavior of goat historical leather treated with hydroxyapatite (HA) and polyethylene glycol 400 (PEG400) was studied and compared with the mechanical properties of untreated sample (control). The samples were subjected to a dynamic tensile stress by dynamic mechanical thermal analysis (DMTA) as well as static stress by tensile test. In addition, the treatment effects on the leather mechanical properties were investigated after accelerating aging test. It was shown that treated sample exhibited more softness, better mechanical properties and less structural changes than the untreated sample. The Scanning Electron Microscopy studies show uniform distribution of nanoparticles in the leather matrix as well as the nano hydroxyapatite particles, which are placed between collagen fibers. Note de contenu : - MATERIALS AND METHODS : Aging procedure - CHARACTERIZATION : Tensile test - Dynamic mechanical thermal analysis (DMTA) - Scanning electron microscopy (SEM-EDX) study - Transition electron microscopy (TEM) study - RESULTS AND DISCUSSION : Tensile strength test - Dynamical mechanical thermal analysis (DMTA) - SEM - EDX - TEM En ligne : https://drive.google.com/file/d/1HS0UnJDyZ404M7OROEhdGZIf-XzjOWM5/view?usp=drive [...] Format de la ressource électronique : Pdf Permalink : https://e-campus.itech.fr/pmb/opac_css/index.php?lvl=notice_display&id=20058 [article]

Réservation

Réserver ce document

Exemplaires (1)

Code-barres	Cote	Support	Localisation	Section	Disponibilité
15840	-	Périodique	Bibliothèque principale	Documentaires	Disponible

---

1 (1 - 1 / 1)