Titre : |
Tripigmented anticorrosive coatings based on lamellar zinc as inhibitor |
Type de document : |
texte imprimé |
Auteurs : |
A. M. Pereyra, Auteur ; Juan G. Castano, Auteur ; Félix EcheverrÃa, Auteur ; L. K. Herrera, Auteur ; Carlos A. Giudice, Auteur |
Année de publication : |
2006 |
Article en page(s) : |
p. 245-249 |
Note générale : |
Bibliogr. |
Langues : |
Anglais (eng) |
Catégories : |
Anticorrosifs Composés lamellaires Concentration pigmentaire volumique Essais de brouillard salin Inhibiteurs (chimie) Pigments Primaire (revêtement) Statistique Zinc
|
Index. décimale : |
667.9 Revêtements et enduits |
Résumé : |
The objective of this work was to study the behaviour of zinc primers, containing either lamellar zinc alone or lamellar zinc mixed with an extender or with an extender/inhibitor mixture. Several formulations of coatings were designed. Accelerated tests were carried out by means of a salt-spray (fog) chamber and a 100% relative humidity cabinet. A statistical analysis was performed considering simultaneous ways of dry-film blistering resistance and anticorrosive behaviour. Results indicated that it was possible to incorporate an extender of high-oil absorption as a spacer of the lamellar zinc particles and also an inhibitor to improve the performance. |
Note de contenu : |
- Formulation and manufacture of primers : Inhibiting pigment and extender - Film-forming material - Pigment composition - Pigment volume concentration - Pigment dispersion
- Experimental method
- Table 1 : Characteristics of metallic zinc inhibiting pigment and extender
- Table 2 : Identification of modified primers
- Table 3 : Composition of sealer, percentage in weight
- Table 4 : Lamellar zinc-rich coatings. Salt fog chamber (ASTM B 117, 1500 hours). Degree of rusting, ASTM D 1654
- Table 5 : Modified lamellar zinc. Salt fog chamber (ASTM B 117, 1500 hours). Degree of rusting, ASTM D 1654
- Table 6 : Lamellar zinc-rich coatings. 100 % relative humidity chamber (ASTM D 2247, 5OO hours). Degree of blistering, ASTM D 714
- Table 7 : Modified lamellar zinc. 100 % relative humidity chamber (ASTM D 2247, 500 hours). Degree of blistering, ASTM D 714
- Table 8 : Sum values of degree of rusting and degree of blistering for the lamellar zinc primers |
DOI : |
10.1007/BF02699667 |
En ligne : |
https://link.springer.com/content/pdf/10.1007/BF02699667.pdf |
Format de la ressource électronique : |
Pdf |
Permalink : |
https://e-campus.itech.fr/pmb/opac_css/index.php?lvl=notice_display&id=5284 |
in SURFACE COATINGS INTERNATIONAL. PART B : COATINGS TRANSACTIONS > Vol. 89, B3 (09/2006) . - p. 245-249