Surface quenching induced microstructure transformations in extrusion foaming of porous sheets / A. Gandhi in INTERNATIONAL POLYMER PROCESSING, Vol. XXX, N° 3 (07/2015)
[article]
Titre : Surface quenching induced microstructure transformations in extrusion foaming of porous sheets Type de document : texte imprimé Auteurs : A. Gandhi, Auteur ; Naresh Bhatnagar, Auteur Année de publication : 2015 Article en page(s) : p. 397-402 Note générale : Bibliogr. Langues : Anglais (eng) Catégories : Caractérisation
Matières plastiques -- Refroidissement
Morphologie (matériaux)
Mousses plastiques -- Extrusion
Polymères -- Surfaces
Surfaces (technologie)Index. décimale : 668.4 Plastiques, vinyles Résumé : In this article, a new technology is described to manufacture open cell thermoplastic foamed sheets with the aid of surface-quenching phenomenon during an extrusion process. As the gas laden polymer extrudate exits the slit die, its surface is rapidly quenched which results in freezing of cells on the surface, while the cells at the core continue to grow and leads to development of open-cellular microstructure at the core. Influence of chill roll temperature was found to be extremely significant in developing porous morphological attributes. Subsequently, synergistic effect of physical blowing agent (N2) content and chill roll temperature was examined for their expansion ratio and foam thickness. Fascinatingly, with reduced chill roll temperatures open-cell microstructure and high expansion ratio was obtained although its thickness was observed to decrease. Further, influence of chill roll rotating speed on foam microstructure and expansion ratio was studied. Lower chill roll rotational speed resulted in development of open-cellular microstructure; while at higher speeds, closed cell morphology was obtained. The results coherently demonstrate that by controlling the chill roll temperatures ; open-cellular microstructure can be developed in sheet extrusion foaming process. Note de contenu : - EXPERIMENTAL : Materials - Foaming methodology - Foam characterization
- RESULTS AND DISCUSSIONS : Influence of surface quenching on foam morphology - Synergistic effect of blowing agent content and surface quenching on open cell microstructure development - Influence of chill roll rotational speed on open cell microstructure developmentDOI : 10.3139/217.3057 En ligne : https://drive.google.com/file/d/1ZdtFspE921BkZifuo1NnEHi5DBDGXFFX/view?usp=drive [...] Format de la ressource électronique : Permalink : https://e-campus.itech.fr/pmb/opac_css/index.php?lvl=notice_display&id=24335
in INTERNATIONAL POLYMER PROCESSING > Vol. XXX, N° 3 (07/2015) . - p. 397-402[article]Réservation
Réserver ce document
Exemplaires (1)
Code-barres Cote Support Localisation Section Disponibilité 17309 - Périodique Bibliothèque principale Documentaires Disponible