Cationic UV-cured epoxy coating with inhibitor-loaded nanoparticles: photoinitiated cationic polymerization, mechanical properties and corrosion protection of steel / Thien Vuong Nguyen in JOURNAL OF COATINGS TECHNOLOGY AND RESEARCH, Vol. 21, N° 3 (05/2024)  

[article]  inJOURNAL OF COATINGS TECHNOLOGY AND RESEARCH > Vol. 21, N° 3 (05/2024) . - p. 1113-1124 Titre : Cationic UV-cured epoxy coating with inhibitor-loaded nanoparticles: photoinitiated cationic polymerization, mechanical properties and corrosion protection of steel Type de document : texte imprimé Auteurs : Thien Vuong Nguyen, Auteur ; Vy Do Truc, Auteur ; Tuan Anh Nguyen, Auteur ; Dai Lam Tran, Auteur Année de publication : 2024 Article en page(s) : p. 1113-1124 Note générale : Bibliogr. Langues : Américain (ame) Catégories : Acier L'acier est un alliage métallique utilisé dans les domaines de la construction métallique et de la construction mécanique. L'acier est constitué d'au moins deux éléments, le fer, très majoritaire, et le carbone, dans des proportions comprises entre 0,02 % et 2 % en masse1. C'est essentiellement la teneur en carbone qui confère à l'alliage les propriétés du métal qu'on appelle "acier". Il existe d’autres métaux à base de fer qui ne sont pas des aciers comme les fontes et les ferronickels par exemple. Anticorrosifs Caractérisation Dioxyde de silicium Enrobage (technologie) Epoxydes Essais de brouillard salin Formulation (Génie chimique) Inhibiteurs (chimie) Métaux -- Revêtements protecteurs Nanoparticules Photoamorceurs (chimie) Polyaddition Revêtements -- Propriétés mécaniques Revêtements organiques Index. décimale : 667.9 Revêtements et enduits Résumé : This work aims to explore how the cationic UV-curing technology can be applied for corrosion protection of metals. For this purpose, the cationic UV-curing epoxy coating is prepared on the steel surface, with addition of the inhibitor-loaded nanoparticles. To reveal the effect of Ce-loaded SiO2 nanoparticles on the photoinitiated cationic polymerization of epoxy coating, various measurements have been carried out during the UV irradiation, such as the consumption of photoinitiator (triarylsulfonium hexafluoroantimonate salts, TAS), conversion of epoxy groups, gel fraction, swelling degree and relative hardness of coating samples. To evaluate the effect of Ce-loaded SiO2 nanoparticles on mechanical and anticorrosion properties of UV-cured epoxy coating, the impact strength, abrasion resistance, electrochemical impedance spectroscopy and salt spray tests have been carried out and analyzed. The experimental data indicate that the incorporation of Ce-loaded SiO2 nanoparticles into epoxy matrix reduces both the relative hardness, gel fraction and the conversion of TAS photoinitiator and epoxy groups. However, the presence of these nanoparticles increases both impact strength, abrasion resistance and anticorrosion performance of the cationic UV-cured epoxy coating. Note de contenu : - EXPERIMENTAL SECTION : Materials - Fabrication of cationic UV-curing epoxy coatings - Coating characterization - RESULTS AND DISCUSSIONS : UV-initiated cationic polymerization of epoxy coating - Morphology and mechanical properties of cationic UV-cured epoxy coatings - Effect of SiO2@Ce3+ nanoparticles on the corrosion protection of UV-cured epoxy coating - Salt spray test - Table 1 : Coating formulations of the cationic UV-curing epoxy coatings DOI : https://doi.org/10.1007/s11998-023-00878-0 En ligne : https://link.springer.com/content/pdf/10.1007/s11998-023-00878-0.pdf Format de la ressource électronique : Pdf Permalink : https://e-campus.itech.fr/pmb/opac_css/index.php?lvl=notice_display&id=41080 [article]

Réservation

Réserver ce document

Exemplaires (2)

Code-barres	Cote	Support	Localisation	Section	Disponibilité
24737	-	Périodique	Bibliothèque principale	Documentaires	Disponible
24688	-	Périodique	Bibliothèque principale	Documentaires	Disponible

---

1 (1 - 1 / 1)