Fabrication of soybean oil-based polyol modified polyurethane foam from ammonium polyphosphate and its thermal stability and flame retardant properties / Xu Zhang in INTERNATIONAL POLYMER PROCESSING, Vol. 39, N° 1 (2024)  

[article]  inINTERNATIONAL POLYMER PROCESSING > Vol. 39, N° 1 (2024) . - p. 32-46 Titre : Fabrication of soybean oil-based polyol modified polyurethane foam from ammonium polyphosphate and its thermal stability and flame retardant properties Type de document : texte imprimé Auteurs : Xu Zhang, Auteur ; Zhaoqian Wang, Auteur ; Simiao Sun, Auteur ; Dehe Yuan, Auteur ; Yueqi Wen, Auteur ; Zhanpeng Su, Auteur ; Zhi Wang, Auteur ; Hua Xie, Auteur Année de publication : 2024 Article en page(s) : p. 32-46 Note générale : Bibliogr. Langues : Anglais (eng) Catégories : Ignifugeants Composé chimique utilisé pour réduire l'inflammabilité. Il peut être incorporé au produit durant sa fabrication ou appliqué ultérieurement à sa surface. Mousses plastiques Mousses plastiques -- Propriétés thermiques Polyols Polyphosphate d'ammonium Polyuréthanes Soja et constituants Stabilité thermique Index. décimale : 668.4 Plastiques, vinyles Résumé : Rigid polyurethane foams (RPUFs) were prepared using biomass soybean oil-based polyol and ammonium polyphosphate (APP) as raw materials. The effects of APP on the thermal stability and combustion performance of soybean oil-based polyol-modified RPUFs were investigated by thermogravimetric analysis, pyrolysis kinetic analysis, limiting oxygen index (LOI) test, cone calorimetry (CONE), scanning electron microscopy (SEM), and smoke density (Ds). The results showed that the modified RPUF with 20 wt% APP (RPUF-S3-20) had the lowest mass loss, the highest integrated programmed decomposition temperature and the highest activation energy. In addition, RPUF-S3-20 had the lowest Ds (30.9), the highest light transmittance (61.4 %), the lowest heat release rate (602.7 kW/m2, 506.8 MJ/m2, and 847.3 kW/m2) and the total heat release (18.3 MJ/m2, 21.4 MJ/m2, and 31.4 MJ/m2), which showed that RPUF-S3-20 had good thermal stability and flame retardant performance. The current results can provide an effective reference for the preparation of environmentally friendly RPUF by bio-based modification. Note de contenu : - EXPERIMENTS : Materials - Preparation of APP modified soybean oil-based polyol RPUF - Measurement and characterization - RESULTS AND DISCUSSION : Thermogravimetric analysis - IPDP analysis - Pyrolysis kinetic analysis - LOI test - Cone analysis - SEM analysis - Smoke density - Flame retardant mechanism DOI : https://doi.org/10.1515/ipp-2023-4399 En ligne : https://drive.google.com/file/d/16IHExDACd5geWe7R0koQf4ckrTo5g7ah/view?usp=drive [...] Format de la ressource électronique : Pdf Permalink : https://e-campus.itech.fr/pmb/opac_css/index.php?lvl=notice_display&id=40849 [article]

Réservation

Réserver ce document

Exemplaires (1)

Code-barres	Cote	Support	Localisation	Section	Disponibilité
24673	-	Périodique	Bibliothèque principale	Documentaires	Disponible

---

1 (1 - 1 / 1)