Enhancing mechanical and thermal properties of unsaturated polyester resin with luffa fiber reinforcements : a volumetric analysis / Nafaa Hameed Sohaib in REVUE DES COMPOSITES ET DES MATERIAUX AVANCES, Vol. 33, N° 6 (12/2023)  

[article]  inREVUE DES COMPOSITES ET DES MATERIAUX AVANCES > Vol. 33, N° 6 (12/2023) . - p. 357-362 Titre : Enhancing mechanical and thermal properties of unsaturated polyester resin with luffa fiber reinforcements : a volumetric analysis Type de document : texte imprimé Auteurs : Nafaa Hameed Sohaib, Auteur ; Bdaiwi Salih Waleed, Auteur Année de publication : 2023 Article en page(s) : p. 357-362 Note générale : Bibliogr. Langues : Anglais (eng) Catégories : Composites à fibres végétales -- Propriétés mécaniques Composites à fibres végétales -- Propriétés physiques Dureté (matériaux) Essais dynamiques Fibres de luffa Isolation thermique Polyesters insaturés Les résines de polyesters insaturés (UP) sont obtenues par polycondensation d’un ou de plusieurs diacides avec un ou plusieurs glycols, l’un, au moins, des constituants contenant une double liaison éthylénique susceptible de réagir ultérieurement sur un composé vinylique, acrylique ou allylique. Par le terme résine polyester, on désigne en fait la dissolution du prépolymère polyester insaturé dans un solvant copolymérisable, le plus utilisé étant le styrène. C’est sous cette forme liquide que les résines polyesters sont livrées aux transformateurs. Après addition de différents adjuvants, charges et renforts, divers procédés de transformation provoquent, sous l’action d’un système catalytique approprié, la copolymérisation finale de la résine en un objet thermodurcissable. Les polyesters insaturés sont d’un usage relativement ancien (1950), essentiellement dans le bâtiment (moulage au contact). Ils ont connu un renouveau important à partir de 1980, en particulier au niveau des formulations et de la fiabilité des procédés grâce au développement de technologies industrielles de moulage par injection et par compression dans l’industrie automobile. Résistance à la compression Résistance au chocs Thermocinétique Index. décimale : 668.4 Plastiques, vinyles Résumé : This study investigates the influence of Luffa Fiber (LF) inclusions on the mechanical and thermal characteristics of unsaturated polyester resin composites. LFs, manually extracted from luffa plants, are integrated at volumetric fractions of 10%, 15%, 20%, and 25% into the resin using a hand lay-up technique at ambient conditions. Subsequent machining prepares the samples for mechanical analysis. It is observed that mechanical properties enhance progressively with increased LF incorporation. The optimal impact resistance reaches 2.34KJ/m2, with maximum hardness and compressive strength values of 81.5N/mm2 and 43.9MPa, respectively. Concurrently, a notable reduction in thermal conductivity is evident, particularly at the 25% LF volume, where it measures approximately 0.105W/m.℃. These findings indicate that the LF-reinforced polyester composites exhibit potential for varied engineering applications. Particularly, their augmented mechanical robustness suits components such as sofa parts and door handles, while their improved thermal insulation properties render them suitable for building insulation. This investigation underscores the viability of LF as a reinforcing agent in polymeric composites, offering a balance of enhanced mechanical strength and thermal efficiency, thereby broadening the scope of their application in engineering domains. Note de contenu : - Materials used : The matrix material (unsaturated polyester) - Reinforcement material - Sample preparation - Mechanical tests : Impact test - Hardness test - The compression test - Physical properties : Thermal conductivity - Impact test - Hardness test - Compressive test - Thermal conductivity test - Table 1 : Experimental results of mechanical and physical tests DOI : https://doi.org/10.18280/rcma.330602 En ligne : https://www.iieta.org/download/file/fid/115604 Format de la ressource électronique : Pdf Permalink : https://e-campus.itech.fr/pmb/opac_css/index.php?lvl=notice_display&id=40763 [article]

Réservation

Réserver ce document

Exemplaires (1)

Code-barres	Cote	Support	Localisation	Section	Disponibilité
24782	-	Périodique	Bibliothèque principale	Documentaires	Disponible

---

1 (1 - 1 / 1)