Preparation, mechanical and thermal properties of polydimethylsiloxane coating for synthetic leathers / Zhe Sun in JOURNAL OF COATINGS TECHNOLOGY AND RESEARCH, Vol. 19, N° 6 (11/2022)  

[article]  inJOURNAL OF COATINGS TECHNOLOGY AND RESEARCH > Vol. 19, N° 6 (11/2022) . - p. 1743-1755 Titre : Preparation, mechanical and thermal properties of polydimethylsiloxane coating for synthetic leathers Type de document : texte imprimé Auteurs : Zhe Sun, Auteur ; Jiating Wen, Auteur ; Jinping Guan, Auteur ; Haojun Fan, Auteur ; Jian Fang, Auteur ; Yi Chen, Auteur ; Wenkai Wang, Auteur ; Qiang Gao, Auteur Année de publication : 2022 Article en page(s) : p. 1743-1755 Note générale : Bibliogr. Langues : Américain (ame) Catégories : Cuir synthétique Enrobage (technologie) Polydiméthylsiloxane Le polydiméthylsiloxane —[O-Si(CH3)2]n—, ou poly(diméthylsiloxane) selon la nomenclature systématique, communément appelé PDMS ou diméthicone, est un polymère organominéral de la famille des siloxanes souvent présent dans les shampoings. On l'y ajoute pour augmenter le volume des cheveux mais il peut également aller boucher les pores du cuir chevelu et rendre les cheveux gras. C'est une des raisons pour lesquelles se laver les cheveux tous les jours est très déconseillé avec un shampooing contenant des silicones. Il existe également de l'amodiméthicone, qui est un dérivé du diméthicone. Le polydiméthylsiloxane est un additif alimentaire (E900), utilisé comme antimoussant dans les boissons (Coca-Cola BlāK). La chaîne de poly(diméthylsiloxane) forme également la structure de base des huiles et des caoutchoucs silicones. Réticulation (polymérisation) Revêtements -- Propriétés mécaniques Revêtements -- Propriétés thermiques Revêtements organiques Index. décimale : 667.9 Revêtements et enduits Résumé : The curing process of polydimethylsiloxane (PDMS) coating was systematically investigated by nonisothermal differential scanning calorimeter (DSC), and accordingly, the thermodynamic as well as kinetic parameters were obtained. Meanwhile, effect of structural factors, including different divinyl-terminated polydimethylsiloxane (ViPDMSVi), divinyl-terminated polymethylvinylsiloxane (ViPMVSVi), polymethylhydrosiloxane (PMHS), and reinforcing filler content, on mechanical and thermal properties of coating was studied. The results demonstrated that platinum compounds could significantly accelerate the hydrosilylation and reduce the curing temperature and activation energy. The viscosity, vinyl/hydrogen sites, and quantities of ViPDMSVi, ViPMVSVi, and PMHS were important factors to influence mechanical and thermal properties. Low viscosity ViPDMSVi and PMHS with side hydrogen atoms could increase crosslinking density, and then enhance the tensile strength and heat resistance. ViPMVSVi with higher viscosity and vinyl content could dramatically improve tensile strength while maintaining breaking elongation. Reinforcing filler was another vital factor to enhance strength and thermostability. 550% improvement in tensile strength occurred when reinforcing filler content was 40 wt%. All aforementioned results provided a comprehensive guidance for the preparation and property regulation of PDMS coating. This kind of PDMS coating can be applied in synthetic leather manufacturing. Note de contenu : - EXPERIMENTAL : Materials - Preparation of polydimethylsiloxane (PDMS) coating - Measurements - RESULTS AND DISCUSSION : Curing thermodynamics and kinetics of PDMS coating - Effect of different ViPDMSVi on mechanical and thermal properties - Effect of hydrogen-containing polydimethylsiloxane on mechanical and thermal properties - Effect of different ViPMVSVi on mechanical and thermal properties - Effect of reinforcing filler on mechanical and thermal properties - Performance of PDMS coating - Performance of PDMS-based synthetic leather DOI : https://doi.org/10.1007/s11998-022-00645-7 En ligne : https://link.springer.com/content/pdf/10.1007/s11998-022-00645-7.pdf?pdf=button Format de la ressource électronique : Pdf Permalink : https://e-campus.itech.fr/pmb/opac_css/index.php?lvl=notice_display&id=38494 [article]

Réservation

Réserver ce document

Exemplaires (1)

Code-barres	Cote	Support	Localisation	Section	Disponibilité
23804	-	Périodique	Bibliothèque principale	Documentaires	Disponible

---

1 (1 - 1 / 1)