Organosilicon leather coating technology based on carbon peak strategy / Wenkai Wang in JOURNAL OF LEATHER SCIENCE AND ENGINEERING, Vol. 4 (Année 2022)  

[article]  inJOURNAL OF LEATHER SCIENCE AND ENGINEERING > Vol. 4 (Année 2022) . - 11 p. Titre : Organosilicon leather coating technology based on carbon peak strategy Type de document : texte imprimé Auteurs : Wenkai Wang, Auteur ; Haojun Fan, Auteur ; Lijiang Song, Auteur ; Zhenya Wang, Auteur ; Heng Li, Auteur ; Jun Xiang, Auteur ; Qiang Huang, Auteur ; Xiangquan Chen, Auteur Année de publication : 2022 Article en page(s) : 11 p. Note générale : Bibliogr. Langues : Anglais (eng) Catégories : Caractérisation Cuir synthétique Gaz à effet de serre -- Réduction Polydiméthylsiloxane Le polydiméthylsiloxane —[O-Si(CH3)2]n—, ou poly(diméthylsiloxane) selon la nomenclature systématique, communément appelé PDMS ou diméthicone, est un polymère organominéral de la famille des siloxanes souvent présent dans les shampoings. On l'y ajoute pour augmenter le volume des cheveux mais il peut également aller boucher les pores du cuir chevelu et rendre les cheveux gras. C'est une des raisons pour lesquelles se laver les cheveux tous les jours est très déconseillé avec un shampooing contenant des silicones. Il existe également de l'amodiméthicone, qui est un dérivé du diméthicone. Le polydiméthylsiloxane est un additif alimentaire (E900), utilisé comme antimoussant dans les boissons (Coca-Cola BlāK). La chaîne de poly(diméthylsiloxane) forme également la structure de base des huiles et des caoutchoucs silicones. Revêtements -- Propriétés mécaniques Revêtements organiques Silylation La silylation est l'introduction d'un groupe silyle, généralement substitué (R3Si–), dans une molécule. Index. décimale : 675 Technologie du cuir et de la fourrure Résumé : Based on the demand of carbon peak and carbon emission reduction strategy, divinyl-terminated polydimethylsiloxane (ViPDMSVi), poly(methylhydrosiloxane) (PMHS), divinyl-terminated polymethylvinylsiloxane (ViPMVSVi), and fumed silica were used as primary raw materials, polydimethylsiloxane (PDMS) synthetic leather coating was in situ constructed by thermally induced hydrosilylation polymerization on the synthetic leather substrate. The effect of the viscosity of ViPDMSVi, the active hydrogen content of PMHS, the molar ratio of vinyl groups to active hydrogen, the dosage of ViPMVSVi and fumed silica on the performance of PDMS polymer coating, including mechanical properties, cold resistance, flexural resistance, abrasion resistance, hydrophobic and anti-fouling properties were investigated. The results show that ViPDMSVi with high vinyl content and PMHS with low active hydrogen content is more conducive to obtaining organosilicon coating with better mechanical properties, the optimized dosage of ViPMVSVi and fumed silica was 7 wt% and 40 wt%, respectively. In this case, the tensile strength and the broken elongation of the PDMS polymer coating reached 5.96 MPa and 481%, showing reasonable mechanical properties for leather coating. Compared with polyurethane based or polyvinyl chloride based synthetic leather, the silicon based synthetic leather prepared by this method exhibits excellent cold resistance, abrasion resistance, super hydrophobicity, and anti-fouling characteristics. Note de contenu : - EXPERIMENTAL : Materials - Preparation of PDMS synthetic leather - Characterization - RESULTS AND DISCUSSION : FT-IR analysis of PDMS polymer film - Mechanical properties of PDMS polymer coating - Characteristics of PDMS synthetic leather coating - Table 1 : Surface energy and their parameters of the test liquids - Table 2 : Effect of ViPDMSVi viscosity on mechanical properties of PDMS polymer film - Table 3 : Effect of ViPDMSVi mixture with different viscosity on mechanical properties of PDMS polymer film - Table 4 : Effect of active hydrogen content on mechanical properties of PDMS polymer film - Table 5 : Effect of molar ratio of vinyl groups to active hydrogen on mechanical properties of PDMS polymer film - Table 6 : Effect of ViPMVSVi mass fraction on mechanical properties of PDMS polymer film - Table 7 : Effect of fumed silica mass fraction on mechanical properties of PDMS polymer film DOI : https://doi.org/10.1186/s42825-022-00101-7 En ligne : https://link.springer.com/content/pdf/10.1186/s42825-022-00101-7.pdf Format de la ressource électronique : Pdf Permalink : https://e-campus.itech.fr/pmb/opac_css/index.php?lvl=notice_display&id=38221 [article]

Exemplaires

Code-barres	Cote	Support	Localisation	Section	Disponibilité
aucun exemplaire

---

1 (1 - 1 / 1)