Comparative study of fire-resistant coatings based on high and low molecular weight tannins / J. Ramirez in JOURNAL OF COATINGS TECHNOLOGY AND RESEARCH, Vol. 19, N° 2 (03/2022)  

[article]  inJOURNAL OF COATINGS TECHNOLOGY AND RESEARCH > Vol. 19, N° 2 (03/2022) . - p. 453–465 Titre : Comparative study of fire-resistant coatings based on high and low molecular weight tannins Type de document : texte imprimé Auteurs : J. Ramirez, Auteur ; M. E. Berrio, Auteur ; A. Diaz-Gomez, Auteur ; L. F. Montoya, Auteur ; A. F. Jaramillo, Auteur ; C. Montalba, Auteur ; K. Fernàndez, Auteur ; C. Medina, Auteur ; M. F. Meléndrez, Auteur Année de publication : 2022 Article en page(s) : p. 453–465 Note générale : Bibliogr. Langues : Américain (ame) Catégories : Caractérisation Catéchine La catéchine est une molécule de la famille des flavonoïdes de la sous-classe des flavanols. Elle est aussi connue sous le nom de catéchol, avec le risque de confusion avec le pyrocatéchol parfois dénommé lui aussi catéchol. L’usage dans la communauté scientifique a fini par imposer le terme de catéchine, dérivé du terme anglais catechin. Initialement découverte dans les fruits de l'acacia à cachou (Acacia catechu) duquel elle dérive son nom, la catéchine et ses nombreux isomères sont de puissants antioxydants qui aident à prévenir les maladies inflammatoires et coronariennes. Le terme de catéchine est aussi parfois utilisé pour désigner la classe des flavanols (flavan-3-ols, flavan-3,4-ols et leurs esters galliques). Pour éviter la confusion entre la classe et le composé, ce dernier est désigné dans ce contexte par (+/-)-catéchine. Enrobage (technologie) Extraction (chimie) Formulation (Génie chimique) Ignifugeants Composé chimique utilisé pour réduire l'inflammabilité. Il peut être incorporé au produit durant sa fabrication ou appliqué ultérieurement à sa surface. Poids moléculaires Revêtements -- Propriétés filmogènes Revêtements -- Propriétés mécaniques Revêtements en phase aqueuse -- Additifs Revêtements protecteurs Tanins Taxifoline La taxifoline ou dihydroquercétine est un composé organique de la famille des flavanonols, un sous-groupe de flavonoïdes. Elle est naturellement présent dans l'açaï (Euterpe oleracea), le mélèze de Sibérie (Larix sibirica) et la silymarine extraite des graines de chardon-Marie. Elle est aussi présente en faible quantité dans l'oignon rouge. C'est le dérivé 2,3-dihydrogéné de la quercétine. Index. décimale : 667.9 Revêtements et enduits Résumé : In order to provide adequate fire resistance to construction materials, such as steel and wood, the use of high and low molecular weight tannins (TMw-H and TMw-L), extracted from the bark of Pinus radiata, as carbonaceous agents, was studied. The extracts were fully characterized by GPC, HPLC, and UV to determine the total amount of phenols, percentage of the monomers, and total yield. The molecular weights of both extracts varied between 2986 and 5573 Da, and they were mainly composed of catechin and taxifolin. Eco-friendly water-based formulations were obtained, without producing volatile organic compounds (VOCs), by varying the extract content between 15.5 and 37.8% w/w. The coatings, varying in thickness and substrates, were evaluated for their film-forming properties, covering power, mechanical properties, such as adhesion, embossing, abrasion, and flexibility, as well as their resistance to fire. The results indicated that good mechanical properties were obtained when using coatings containing TMw-L compared with those obtained when using TMw-H. The carbonization index (28%) and the mass loss percentage (9.35%) of the coatings containing TMw-L compared well to commercial coatings, indicating that they have excellent fire-retardant properties. However, the behavior of the TMw-H containing coatings was rather intumescent. Note de contenu : - MATERIALS AND METHODS : Extraction and characterization of the TMw-H and TMw-L - Formulation of coatings and surface preparation of steel and wood substrates - Evaluation of the mechanical properties of the coatings - Fire-resistant behavior - RESULTS AND DISCUSSION : Characterization of the tannin extracts obtained from the bark of Pinus radiata - Formulation of coatings - Evaluation of the coating properties - Evaluation of the fire-resistant properties of the coatings - Table 1 : Variation of the percentage of the compositions in the formulations for TMw-L and TMw-H - Table 2 : Characterization of the tannin extracts obtained from the bark of Pinus radiata - Table 3 : PVC, CPVC, and λ values for the formulations - Table 4 : Evaluation of film properties of formulations and commercial coatings - Table 5 : Evaluation of the mechanical properties of the coatings - Table 6 : Mass loss and carbonization index of the coatings DOI : https://doi.org/10.1007/s11998-021-00532-7 En ligne : https://link.springer.com/content/pdf/10.1007/s11998-021-00532-7.pdf Format de la ressource électronique : Pdf Permalink : https://e-campus.itech.fr/pmb/opac_css/index.php?lvl=notice_display&id=37277 [article]

Réservation

Réserver ce document

Exemplaires (1)

Code-barres	Cote	Support	Localisation	Section	Disponibilité
23408	-	Périodique	Bibliothèque principale	Documentaires	Disponible

---

1 (1 - 1 / 1)