The effect of silica nanofiller on the physical and thermal characteristics of rubber-based composites / A. Chelli in INTERNATIONAL POLYMER PROCESSING, Vol. 36, N° 1 (2021)  

[article]  inINTERNATIONAL POLYMER PROCESSING > Vol. 36, N° 1 (2021) Titre : The effect of silica nanofiller on the physical and thermal characteristics of rubber-based composites Type de document : texte imprimé Auteurs : A. Chelli, Auteur ; L. Hemmouche, Auteur ; H. Ait-Sadi, Auteur ; D. Trache, Auteur ; M. Benziane, Auteur ; R. Ait-Sadi, Auteur Année de publication : 2021 Note générale : Bibliogr. Langues : Anglais (eng) Catégories : Analyse morphologique Calorimétrie Caoutchouc Caoutchouc nitrile-butadiène Caractérisation Composites -- Propriétés mécaniques Composites -- Propriétés thermiques Dureté (matériaux) Essais dynamiques Formulation (Génie chimique) Nanoparticules Silice La silice est la forme naturelle du dioxyde de silicium (SiO2) qui entre dans la composition de nombreux minéraux. La silice existe à l'état libre sous différentes formes cristallines ou amorphes et à l'état combiné dans les silicates, les groupes SiO2 étant alors liés à d'autres atomes (Al : Aluminium, Fe : Fer, Mg : Magnésium, Ca : Calcium, Na : Sodium, K : Potassium...). Les silicates sont les constituants principaux du manteau et de l'écorce terrestre. La silice libre est également très abondante dans la nature, sous forme de quartz, de calcédoine et de terre de diatomée. La silice représente 60,6 % de la masse de la croûte terrestre continentale. Index. décimale : 668.4 Plastiques, vinyles Résumé : The use of nano composites in elastomer blends gives outstanding mechanical properties compared to the use of micro and macro composites, even with very low nano filler content. In this paper, we studied the influence of varying proportions of natural rubber (NR) and acrylonitrile butadiene rubber (NBR) reinforced with nano silica on the mechanical and thermal characteristics of the rubber. Mechanical characterizations were carried out with hardness, tensile strength, elongation at break, tear strength, modulus and toughness. For thermal analyses, we used differential scanning calorimetry (DSC) and Thermogravimetric Analysis (TGA). In most cases, the increase in the percentage of NBR with the presence of nano silica enhances hardness, modulus and toughness, however, it reduces tensile strength, tear strength and elongation at break. It was found that nano silica has a catalytic effect on the mixture, and NBR has a catalytic effect on the decomposition of NR. Note de contenu : - EXPERIMENTAL : Materials - Cure characteristics - Mechanical characterization - Morphological analysis - Thermal characterization - RESULTS AND DISCUSSION : Mechanical properties of the rubber samples - Morphological analysis - Thermal proprieties of the rubber samples - Table 1 : Compound formulations - Table 2 : Properties of the rubber vulcanizates - Table 3 : Temperature of onset of degradation and enthalpy of the samples DOI : https://doi.org/10.1515/ipp-2020-3956 En ligne : https://drive.google.com/file/d/1e24UlfuwKoYy4IctQbcwb0VcWJfsyiTC/view?usp=shari [...] Format de la ressource électronique : Pdf Permalink : https://e-campus.itech.fr/pmb/opac_css/index.php?lvl=notice_display&id=36347 [article]

Réservation

Réserver ce document

Exemplaires (1)

Code-barres	Cote	Support	Localisation	Section	Disponibilité
23731	-	Périodique	Bibliothèque principale	Documentaires	Disponible

---

1 (1 - 1 / 1)