Effect of silica based sols on the optical properties and colour fastness of synthetic indigo dyed denim fabrics / Sabiha Sezgin Bozok in COLORATION TECHNOLOGY, Vol. 137, N° 3 (06/2021)  

[article]  inCOLORATION TECHNOLOGY > Vol. 137, N° 3 (06/2021) . - p. 209-216 Titre : Effect of silica based sols on the optical properties and colour fastness of synthetic indigo dyed denim fabrics Type de document : texte imprimé Auteurs : Sabiha Sezgin Bozok, Auteur ; Ramazan Tugrul Ogulata, Auteur Année de publication : 2021 Article en page(s) : p. 209-216 Note générale : Bibliogr. Langues : Anglais (eng) Catégories : 3-Glycidoxypropyltrimethoxysilane Colorimétrie Enrobage (technologie) Essais (technologie) Indigo Jeans Orthosilicate de tétraéthyle L'orthosilicate de tétraéthyle (TEOS) est un composé chimique de formule Si(OCH2CH3)4 ou plus simplement Si(OEt)4; l'abréviation TEOS (pour tetraethylorthosilicate) est généralement utilisée dans l'industrie du sol-gel, où il est intensivement étudié. La majorité des études en sol-gel pour des sols de silices ont utilisé ce produit comme précurseur. Le TEOS est généralement produit par alcoolyse du tétrachlorure de silicium SiCl4 dans de l'éthanol CH3CH2OH : SiCl4 + 4 CH3CH2OH → Si(OCH2CH3)4 + 4 HCl. Il est utilisé pour la réticulation de silicones et possède certaines applications comme précurseur du dioxyde de silicium SiO2 dans l'industrie des semi-conducteurs6 dans le cadre d'une réaction sol-gel. La propriété remarquable du TEOS est en effet de former du SiO2 par simple hydrolyse en libérant de l'éthanol CH3CH2OH : Si(OCH2CH3)4 + 2 H2O → SiO2 + 4 CH3CH2OH. Résistance à l'abrasion Résistance au lavage Silice La silice est la forme naturelle du dioxyde de silicium (SiO2) qui entre dans la composition de nombreux minéraux. La silice existe à l'état libre sous différentes formes cristallines ou amorphes et à l'état combiné dans les silicates, les groupes SiO2 étant alors liés à d'autres atomes (Al : Aluminium, Fe : Fer, Mg : Magnésium, Ca : Calcium, Na : Sodium, K : Potassium...). Les silicates sont les constituants principaux du manteau et de l'écorce terrestre. La silice libre est également très abondante dans la nature, sous forme de quartz, de calcédoine et de terre de diatomée. La silice représente 60,6 % de la masse de la croûte terrestre continentale. Sol-gel, Procédé Solidité de la couleur Teinture -- Fibres textiles Index. décimale : 667.3 Teinture et impression des tissus Résumé : The colour of denim fabric, which has a large share in the textile market, is an important parameter together with comfort properties during usage. While some users prefer the colour of denim fabrics to have different colours as they use them, others want to be provided with colour stability of the fabrics during use. In this study, the effect of a sol-gel technique on indigo dyed denim fabrics was investigated. The aim was to reduce the colour change that occurs in denim fabrics as a result of external factors by using silica-based coatings. The sols were prepared by using TEOS (tetraethylortosilicate) and different volumes of GPTS ((3-glycidyloxypropyl)trimethoxysilane) as precursors in acidic and alkaline conditions. Synthetic indigo dyed cotton denim fabrics were treated with the sols by applying the pad-dry-cure method. It was determined that the colour strength of the treated samples increased and the fabrics treated with the sols prepared in alkaline condition became darker compared to the sols in acidic condition. It is seen that the use of crosslinkers while preparing the sol could improve the rubbing and washing fastness of commercial denim samples. Note de contenu : - MATERIALS AND METHODS : Preparation of the sols and coating process - Testing methods - RESULTS AND DISCUSSION : SEM analysis - Colour measurements - Rubbing fastness - Wash fastness - Table 1 : Content of solutions and the sample codes - Table 2 : Colour difference values of the treated samples - Table 3 : Rubbing fastness of the samples - Table 4 : Washing fastness of the samples according to the standard DOI : https://doi.org/10.1111/cote.12521 En ligne : https://onlinelibrary.wiley.com/doi/epdf/10.1111/cote.12521 Format de la ressource électronique : Pdf Permalink : https://e-campus.itech.fr/pmb/opac_css/index.php?lvl=notice_display&id=36087 [article]

Réservation

Réserver ce document

Exemplaires (1)

Code-barres	Cote	Support	Localisation	Section	Disponibilité
22845	-	Périodique	Bibliothèque principale	Documentaires	Disponible

---

1 (1 - 1 / 1)