The influence of mechanical recycling on properties in injection molding of fiber-reinforced polypropylene / Tim Evens in INTERNATIONAL POLYMER PROCESSING, Vol. XXXIV, N° 4 (08/2019)  

[article]  inINTERNATIONAL POLYMER PROCESSING > Vol. XXXIV, N° 4 (08/2019) . - p. 398-407 Titre : The influence of mechanical recycling on properties in injection molding of fiber-reinforced polypropylene Type de document : texte imprimé Auteurs : Tim Evens, Auteur ; G.-J. Bex, Auteur ; M. Yigit, Auteur ; J. de Keyzer, Auteur ; F. Desplentere, Auteur ; A. van Bael, Auteur Année de publication : 2019 Article en page(s) : p. 398-407 Note générale : Bibliogr. Langues : Anglais (eng) Catégories : Composites à fibres -- Moulage par injection Composites à fibres -- Propriétés mécaniques Composites à fibres -- Recyclage Composites à fibres courtes Composites à fibres de carbone Composites à fibres de verre Composites à fibres végétales Essais dynamiques Lin et constituants Le lin cultivé (Linum usitatissimum) est une plante annuelle de la famille des Linaceae cultivée principalement pour ses fibres, mais aussi pour ses graines oléagineuses. Les fibres du lin permettent de faire des cordes, du tissu (lin textile pour ses qualités anallergiques, isolantes et thermorégulateurs), ou plus récemment des charges isolantes pour des matériaux de construction. Les graines sont utilisées pour produire de l'huile de lin pour l'industrie de l'encre et de la peinture, pour la consommation humaine et animale, à cause de sa richesse en oméga 3. Le lin est une des rares fibres textiles végétales européennes. Elle a comme caractéristiques la légereté, la rigidité et la résistance et comme particularité d'être une fibre longue (plusieurs dizaines de centimètres), par rapport aux fibres courtes (coton, chanvre) ou moyennes (laine). Polypropylène Résistance à la traction Résistance au chocs Rigidité (mécanique) Index. décimale : 668.4 Plastiques, vinyles Résumé : Due to higher mechanical demands on technical parts, the application of short fiber reinforced thermoplastics for injection molding is strongly increasing. Therefore, more attention needs to be paid to the optimization of their recycling processes. Mechanical shredding of thermoplastics into granules is a common recycling method within polymer industries. The breaking of polymer chains and reinforcing fibers during this process may affect the material properties. This study presents the effect of ten recycling sequences on four different materials: polypropylene, glass fiber filled polypropylene, carbon fiber filled polypropylene and flax fiber filled polypropylene. Tests indicate that recycling has a negative influence on most of the mechanical properties. Polypropylene without fibers forms an exception as it does not exhibit any significant change in material properties. Glass fiber and carbon fiber reinforced polypropylene show a decrease in stiffness and tensile strength during the recycling steps. The impact strength of carbon and flax fiber reinforced polypropylene increases whereas that of glass fiber reinforced polypropylene decreases. Note de contenu : - MATERIALS AND METHODS - RESULTS AND DISCUSSION : Tensile strength - Flexural modulus - Impact strength - Stress-strain curve - Effect of recycling on the fiber length distribution - Discussion DOI : 10.3139/217.3770 En ligne : https://www.degruyter.com/document/doi/10.3139/217.3770/pdf Format de la ressource électronique : Pdf Permalink : https://e-campus.itech.fr/pmb/opac_css/index.php?lvl=notice_display&id=33058 [article]

Réservation

Réserver ce document

Exemplaires (1)

Code-barres	Cote	Support	Localisation	Section	Disponibilité
21083	-	Périodique	Bibliothèque principale	Documentaires	Disponible

---

1 (1 - 1 / 1)