Direct electroplating of nickel on ABS plastic using polyaniline–silver surface composite synthesized using different acids / Maryam Mehdizadeh in JOURNAL OF COATINGS TECHNOLOGY AND RESEARCH, Vol. 15, N° 6 (11/2018)  

[article]  inJOURNAL OF COATINGS TECHNOLOGY AND RESEARCH > Vol. 15, N° 6 (11/2018) . - p. 1433-1442 Titre : Direct electroplating of nickel on ABS plastic using polyaniline–silver surface composite synthesized using different acids Type de document : texte imprimé Auteurs : Maryam Mehdizadeh, Auteur ; Mehdi Khorasanian, Auteur ; Seyyed Mohammad Lari Baghal Année de publication : 2018 Article en page(s) : p. 1433-1442 Note générale : Bibliogr. Langues : Américain (ame) Catégories : Adhésion Argent Conduction électrique Dépôt électrolytique Fourier, Spectroscopie infrarouge à transformée de Matières plastiques -- Revêtement Microscopie électronique à balayage Nickel Le nickel est un élément chimique, de symbole Ni et de numéro atomique 28. Le nickel est un métal blanc argenté qui possède un éclat poli. Il fait partie du groupe du fer. C'est un métal ductile (malléable). On le trouve sous forme combinée au soufre dans la millérite, à l'arsenic dans la nickéline. Grâce à sa résistance à l'oxydation et à la corrosion, il est utilisé dans les pièces de monnaie, pour le plaquage du fer, du cuivre, du laiton, dans certaines combinaisons chimiques et dans certains alliages. Il est ferromagnétique, et est fréquemment accompagné de cobalt. Il est particulièrement apprécié pour les alliages qu'il forme. Particules (matières) Polyacrylonitrile Polyaniline Surfaces -- Analyse Terpolymère acrylonitrile butadiène styrène Index. décimale : 667.9 Revêtements et enduits Résumé : Nickel coating was directly electroplated on acrylonitrile butadiene styrene (ABS) plastic substrate using a new method. The substrate surface was first coated by thin polyaniline film, then silver particles were deposited on the surface in order to improve the electrical conductivity. Three different acids (perchloric, nitric, and sulfuric acid) were used to synthesize the primary polyaniline film. The method adopted in the present study was not based on incorporation of silver particles within the polyaniline matrix; rather, the silver was deposited on the substrate surface. The electrical conductivity of the samples was increased to a level high enough for direct electroplating of nickel. The sample synthesized using nitric acid showed the finest grain size (1.57 µm) and greatest thickness of the final nickel coating (57 µm). The sample synthesized using sulfuric acid exhibited the lowest electrical resistance (0.008 Ω). In addition, the nickel coating deposited on the surface of the sample synthesized using perchloric acid exhibited the strongest adhesion to the substrate (5B according to ASTM standard). Note de contenu : - EXPERIMENTAL : Materials - Procedure - Surface characterization - RESULTS AND DISCUSSION : FTIR spectra - Scanning electron microscopy (SEM) - Electrical conductivity - Adhesion DOI : 10.1007/s11998-018-0075-2 En ligne : https://link.springer.com/content/pdf/10.1007%2Fs11998-018-0075-2.pdf Format de la ressource électronique : Pdf Permalink : https://e-campus.itech.fr/pmb/opac_css/index.php?lvl=notice_display&id=31364 [article]

Réservation

Réserver ce document

Exemplaires (1)

Code-barres	Cote	Support	Localisation	Section	Disponibilité
20388	-	Périodique	Bibliothèque principale	Documentaires	Disponible

---

1 (1 - 1 / 1)