Synthesis of acrylate-based UV/thermal dual-cure coatings for antifogging / Bolong Yao in JOURNAL OF COATINGS TECHNOLOGY AND RESEARCH, Vol. 15, N° 1 (01/2018)  

[article]  inJOURNAL OF COATINGS TECHNOLOGY AND RESEARCH > Vol. 15, N° 1 (01/2018) . - p. 149-158 Titre : Synthesis of acrylate-based UV/thermal dual-cure coatings for antifogging Type de document : texte imprimé Auteurs : Bolong Yao, Auteur ; Haiping Zhao, Auteur ; Likui Wang, Auteur ; Yun Liu, Auteur ; Chunsen Zheng, Auteur ; Hongping Li, Auteur ; Changqing Sun, Auteur Année de publication : 2018 Article en page(s) : p. 149-158 Note générale : Bibliogr. Langues : Américain (ame) Catégories : Analyse thermique Angle de contact Caractérisation Fourier, Spectroscopie infrarouge à transformée de Microscopie à force atomique Orthosilicate de tétraéthyle L'orthosilicate de tétraéthyle (TEOS) est un composé chimique de formule Si(OCH2CH3)4 ou plus simplement Si(OEt)4; l'abréviation TEOS (pour tetraethylorthosilicate) est généralement utilisée dans l'industrie du sol-gel, où il est intensivement étudié. La majorité des études en sol-gel pour des sols de silices ont utilisé ce produit comme précurseur. Le TEOS est généralement produit par alcoolyse du tétrachlorure de silicium SiCl4 dans de l'éthanol CH3CH2OH : SiCl4 + 4 CH3CH2OH → Si(OCH2CH3)4 + 4 HCl. Il est utilisé pour la réticulation de silicones et possède certaines applications comme précurseur du dioxyde de silicium SiO2 dans l'industrie des semi-conducteurs6 dans le cadre d'une réaction sol-gel. La propriété remarquable du TEOS est en effet de former du SiO2 par simple hydrolyse en libérant de l'éthanol CH3CH2OH : Si(OCH2CH3)4 + 2 H2O → SiO2 + 4 CH3CH2OH. Photoamorceurs (chimie) Polyacrylates Polymères -- Synthèse Résistance à l'humidité:Résistance à l'eau Résonance magnétique nucléaire Réticulants Revêtements -- Propriétés mécaniques:Peinture -- Propriétés mécaniques Revêtements anti-buée:Peinture anti-buée Index. décimale : 667.9 Revêtements et enduits Résumé : A dual-cure hydrophilic acrylate polymer was synthesized via radical polymerization with acrylic acid (AA), isophorone diisocyanate (IPDI), 2-acrylamide-2-methylpropane sulfonic acid (AMPS), hydroxyethyl acrylate (HEA), and 3-(trimethoxysilyl)propyl-2-methyl-2-methacrylate (MPS) as monomers, then used as prepolymer for antifog coating with tetraethylorthosilicate (TEOS) as a novel crosslinker. The prepolymer was mixed with crosslinking agent and photoinitiator to form coating formulas. The coating was characterized by nuclear magnetic resonance (NMR), Fourier-transform infrared (FTIR) spectroscopy, and contact angle measurements. The results indicated that the dosage of AMPS and TEOS had great influence on the antifog performance. With an increasing TEOS amount, the hardness, adhesion, water resistance, impact resistance, and thermal stability of the films were improved, at the expense of transparency ; with increasing dosage of AMPS, the hydrophilicity of the film increased at the expense of water resistance. Optimum coating properties could be obtained when the amount of AMPS was 7% and that of TEOS was 5.5%. Scanning electron microscopy (SEM) and atomic force microscopy (AFM) results showed that some SiO2 microspheres were formed and microphase separation occurred between the macromolecular segments, yielding the excellent coating properties. Note de contenu : - EXPERIMENTAL : Materials - Preparation of antifog coatings - Characterization - RESULTS AND DISCUSSION : FTIR spectroscopy - 1H and 13C NMR analysis - Water contact angle and water absorption of antifog coatings - Transparency of antifog coatings - Spreading time and contact angle - AFM analysis of antifog coatings - DSC analysis - Mechanical performance and water resistance of coatings - Antifog property of coatings DOI : 10.1007/s11998-017-9966-x En ligne : https://link.springer.com/content/pdf/10.1007%2Fs11998-017-9966-x.pdf Format de la ressource électronique : Pdf Permalink : https://e-campus.itech.fr/pmb/opac_css/index.php?lvl=notice_display&id=30107 [article]

Réservation

Réserver ce document

Exemplaires (1)

Code-barres	Cote	Support	Localisation	Section	Disponibilité
19610	-	Périodique	Bibliothèque principale	Documentaires	Disponible

---

1 (1 - 1 / 1)