Synthesis and characterization of nanoporous sodium-substituted hydrophilic titania ceramics coated on 316L SS for biomedical applications / K. Bavya Devi in JOURNAL OF COATINGS TECHNOLOGY AND RESEARCH, Vol. 8, N° 5 (10/2011)  

[article]  inJOURNAL OF COATINGS TECHNOLOGY AND RESEARCH > Vol. 8, N° 5 (10/2011) . - p. 595-604 Titre : Synthesis and characterization of nanoporous sodium-substituted hydrophilic titania ceramics coated on 316L SS for biomedical applications Type de document : texte imprimé Auteurs : K. Bavya Devi, Auteur ; Kulwant Singh, Auteur ; N. Rajendran, Auteur Année de publication : 2011 Article en page(s) : p. 595-604 Note générale : Bibliogr. Langues : Américain (ame) Catégories : Acier inoxydable Adhésion Angle de contact Biomatériaux Caractérisation Composés inorganiques -- Synthèse Dioxyde de titane Hydrophilie Hydroxyapatite L'hydroxyapatite est une espèce minérale de la famille des phosphates, de formule Ca5(PO4)3(OH), usuellement écrite Ca10(PO4)6(OH)2 pour souligner le fait que la maille de la structure cristalline comprend deux molécules. L'hydroxyapatite est le membre hydroxylé du groupe apatite. L'ion OH- peut être remplacé par le fluor, le chlore ou le carbonate. L'hydroxyapatite cristallise dans le système hexagonal. La poudre d'hydroxyapatite pure est blanche. Celles que l'on trouve dans la nature peuvent cependant être de couleur marron, jaune ou verte. Matériaux poreux Revêtement de céramique Index. décimale : 667.9 Revêtements et enduits Résumé : Bioactive sodium-substituted titania coating on 316L SS substrate was prepared. XRD patterns exhibited the formation of a mixture of two phases (Na2Ti3O7, Na2Ti6O13) with monoclinic structure. FTIR spectra showed that the set of overlapping peaks in the range of 800–400 cm−1 are related to Ti–O and Ti–O–Ti groups. SEM-EDAX, AFM, and TEM showed the surface morphology of the coated surface to be nanoporous and uniform. The influence of the bioactivity of the coating in a simulated body fluid (SBF) medium was examined. Excellent adhesion of the ceramic composites to the substrate was achieved. The hydrophilic nature of the sodium titanate coating induced the formation of hydroxyapatite layer on the metal surface. The corrosion protection performance of the coatings has been evaluated using potentiodynamic polarization and electrochemical impedance spectroscopy measurements, which proved increased corrosion resistance of nanosodium titanate-coated 316L SS. These results imply that the sodium titanate-coated 316L SS acts as a barrier layer to the metallic substrate. Note de contenu : EXPERIMENTAL PROCEDURE : Substrate pretreatments - Synthesis of the coatings. CHARACTERIZATION TECHNIQUES : Surface characterization - Biochemical measurement. RESULTS AND DISCUSSION : Surface characterizations - Mechanical properties - In vitro characterization - Bioelectrochemical corrosion studies. DOI : 10.1007/s11998-011-9344-z En ligne : https://link.springer.com/content/pdf/10.1007%2Fs11998-011-9344-z.pdf Format de la ressource électronique : Pdf Permalink : https://e-campus.itech.fr/pmb/opac_css/index.php?lvl=notice_display&id=12235 [article]

Réservation

Réserver ce document

Exemplaires (1)

Code-barres	Cote	Support	Localisation	Section	Disponibilité
13360	-	Périodique	Bibliothèque principale	Documentaires	Disponible

---

1 (1 - 1 / 1)