Mechanical, curing parameters and water absorption of hybrid date palm leaf-orange peel fibers reinforced unsaturated polyester composites / Hamza Chelali in REVUE DES COMPOSITES ET DES MATERIAUX AVANCES, Vol. 31, N° 3 (06/2021)  

[article]  inREVUE DES COMPOSITES ET DES MATERIAUX AVANCES > Vol. 31, N° 3 (06/2021) . - p. 139-144 Titre : Mechanical, curing parameters and water absorption of hybrid date palm leaf-orange peel fibers reinforced unsaturated polyester composites Type de document : texte imprimé Auteurs : Hamza Chelali, Auteur ; Ahmed Meghezzi, Auteur ; Abir Berkouk, Auteur ; Mohamed Toufik Soltani, Auteur ; George Winning, Auteur Année de publication : 2021 Article en page(s) : p. 139-144 Note générale : Bibliogr. Langues : Français (fre) Catégories : Caractérisation Composites à fibres -- Propriétés physiques Composites à fibres végétales -- Propriétés mécaniques Composites à fibres végétales -- Propriétés thermiques Ecorces d'orange Fibres de palmier dattier Humidité -- Absorption:Eau -- Absorption Polyesters insaturés Les résines de polyesters insaturés (UP) sont obtenues par polycondensation d’un ou de plusieurs diacides avec un ou plusieurs glycols, l’un, au moins, des constituants contenant une double liaison éthylénique susceptible de réagir ultérieurement sur un composé vinylique, acrylique ou allylique. Par le terme résine polyester, on désigne en fait la dissolution du prépolymère polyester insaturé dans un solvant copolymérisable, le plus utilisé étant le styrène. C’est sous cette forme liquide que les résines polyesters sont livrées aux transformateurs. Après addition de différents adjuvants, charges et renforts, divers procédés de transformation provoquent, sous l’action d’un système catalytique approprié, la copolymérisation finale de la résine en un objet thermodurcissable. Les polyesters insaturés sont d’un usage relativement ancien (1950), essentiellement dans le bâtiment (moulage au contact). Ils ont connu un renouveau important à partir de 1980, en particulier au niveau des formulations et de la fiabilité des procédés grâce au développement de technologies industrielles de moulage par injection et par compression dans l’industrie automobile. Thermogravimétrie Index. décimale : 668.4 Plastiques, vinyles Résumé : In this study, polymer-hybrid natural fibers composites were prepared using unsaturated polyester resin (UPR) as the matrix and a filler using date palm leaf fiber (DPLF) and orange peel fiber (OPF). The effect of DPLF and OPF on mechanical behavior (tensile strength and elongation at break), moisture absorption, UPR gel time (tgel) and peak exothermic temperature (Tpeak) were determined. The composites of UPR reinforced with DPLF and OPF were processed by hand lay-up technique. The UPR weight fraction was maintained at 90%, and DPLF/OPF proportions varied so that the percentage of natural fiber was 10 wt%. Seven (07) composites were prepared (C1, C2, C3, C4, C5, C6 and C7) with different DPLF:OPF ratios (0:0, 1:0, 0.75:0.25, 0.5:0.5, 0.33:0.67, 0.25:0.75, 0:1) respectively in order to screen the possible interactions. DPLF were surface modified using 6% Alkali treatment, OPF were used without surface modification. Unlike DPLF, OPF showed considerable increase of UPR tgel and Tpeak which act as natural inhibitor. Tensile strength and fracture strength were also impacted negatively and positively depending on the different fiber proportions. Absorption tests showed a decrease in the composites hydrophobicity which increases significantly with higher DPLF proportions. Note de contenu : - Materials and methods : Materials - Preparation of UPR/DPLF-OPF composites - Characterization - Results and discussion : Curing properties - Mechanical properties - Morphological properties - Thermogravimetric analysis (TGA) - Water uptake - Table 1 : Chemical composition of DPLF - Table 2 : Chemical composition of OPF - Table 3 : Phenolic compounds in Maltease OPF - Table 4 : Curing parameters - Table 5 : Thermal properties DOI : https://doi.org/10.18280/rcma.310304 En ligne : https://www.iieta.org/download/file/fid/56446 Format de la ressource électronique : Pdf Permalink : https://e-campus.itech.fr/pmb/opac_css/index.php?lvl=notice_display&id=37664 [article]

Exemplaires

Code-barres	Cote	Support	Localisation	Section	Disponibilité
aucun exemplaire

---

1 (1 - 1 / 1)