Titre : |
Preparation and characterization of soap-free fluorine-containing acrylate latex |
Type de document : |
texte imprimé |
Auteurs : |
Jin Wang, Auteur ; Xing-rong Zeng, Auteur ; Hong-Qiang Li, Auteur |
Année de publication : |
2010 |
Article en page(s) : |
p. 469-476 |
Note générale : |
Bibliogr. |
Langues : |
Américain (ame) |
Catégories : |
Acrylates Les monomères acrylates sont un groupe d'esters faisant partie des vinyles, car renfermant une double liaison carbone-carbone et sont utilisés pour former des polyacryliques qui ont de multiples usages. Caractérisation Emulsifiants Fluor Latex Polymérisation Spectroscopie de photoélectrons
|
Index. décimale : |
667.9 Revêtements et enduits |
Résumé : |
The soap-free fluorine-containing acrylate latices were prepared by the pre-emulsification and semicontinuous polymerization method, with perfluorooctylethyl methacrylate (PFEA) as fluorinated acrylate monomer and monophosphoric acid allyloxy nonylphenoxy poly(ethyleneoxy)(10) ether as reactive emulsifier. The structure and property of latex polymers were characterized by laser particle size analyzer, attenuated total reflectance spectra of infrared, X-ray photoelectron spectroscopy (XPS), and thermogravimetric analysis. The effects of polymerization conditions on the conversion and polymerization stability were discussed in detail and the optimal polymerization condition was obtained. XPS analysis indicates that the perfluoroalkyl groups have the tendency to enrich at the film–air interface. With the increasing of PFEA amount, the water absorption of the film decreases and the water contact angle of the film increases. At the same time, the thermal stability of the copolymer is greatly enhanced with the increasing of PFEA amount. |
DOI : |
10.1007/s11998-009-9199-8 |
En ligne : |
https://link.springer.com/content/pdf/10.1007%2Fs11998-009-9199-8.pdf |
Format de la ressource électronique : |
Pdf |
Permalink : |
https://e-campus.itech.fr/pmb/opac_css/index.php?lvl=notice_display&id=9769 |
in JOURNAL OF COATINGS TECHNOLOGY AND RESEARCH > Vol. 7, N° 4 (07/2010) . - p. 469-476