[article]
Titre : |
Wood surfaces protected with transparent multilayer UV-cured coatings reinforced with nanosilica and nanoclay. Part II : Application of a standardized test method to study the effect of relative humidity on scratch resistance |
Type de document : |
texte imprimé |
Auteurs : |
William Nguegang Nkeuwa, Auteur ; Bernard Riedl, Auteur ; Véronic Landry, Auteur |
Année de publication : |
2014 |
Article en page(s) : |
p. 993-1011 |
Note générale : |
Bibliogr. |
Langues : |
Américain (ame) |
Catégories : |
Air -- Humidité Argile Bois Bois -- Revêtements Caractérisation Essais (technologie) Essais de résilience Evaluation Nanoparticules Revêtements -- Séchage sous rayonnement ultraviolet:Peinture -- Séchage sous rayonnement ultraviolet Revêtements multicouches SiliceLa silice est la forme naturelle du dioxyde de silicium (SiO2) qui entre dans la composition de nombreux minéraux.
La silice existe à l'état libre sous différentes formes cristallines ou amorphes et à l'état combiné dans les silicates, les groupes SiO2 étant alors liés à d'autres atomes (Al : Aluminium, Fe : Fer, Mg : Magnésium, Ca : Calcium, Na : Sodium, K : Potassium...).
Les silicates sont les constituants principaux du manteau et de l'écorce terrestre. La silice libre est également très abondante dans la nature, sous forme de quartz, de calcédoine et de terre de diatomée. La silice représente 60,6 % de la masse de la croûte terrestre continentale. Statistique
|
Index. décimale : |
667.9 Revêtements et enduits |
Résumé : |
Coated wood surfaces of components constituting flooring and furniture for interior end uses that exhibit good tribological properties are highly desirable. Surfaces of yellow birch wood (Betula alleghaniensis Britton) were protected with six different types of multilayer coatings (MCs) developed in this study. Each MC consisted of three layers: primer, sealer, and topcoat. UV-curable primer and topcoat formulations were, respectively, reinforced with a hydrophobic fumed silica (NS: 0 and 0.5 wt% in the formulation) and nanoclay (NC: 0, 1, and 3 wt% in the formulation). The scratch resistance of MCs on wood surfaces conditioned at 40% and 80% relative humidity (RH) was quantitatively and qualitatively studied. Quantitative evaluation was performed according to a standardized scratch test, while scanning electron microscopy (SEM) analysis was used for qualitative evaluation. Statistical results have shown that NS, NC, and NS × NC do not have a significant effect on scratch resistance of coated wood surfaces, whereas the effect of RH is significant. Regardless of RH, SEM images reveal that: (i) there is no sign of lack of adhesion between coating layers and the MCs/wood surfaces interface and (ii) all the MCs seem to have a ductile/brittle response to scratching. Qualitative information was in accordance with quantitative results. |
Note de contenu : |
- EXPERIMENTAL : Materials - Statistical design - Wood surface preparation - Formulations application and UV-curing processes - Preparation and conditioning of coated wood samples - Characterization - Statistical analysis
- RESULTS AND DISCUSSION : Quantitative evaluation of scratch resistance of multilayer coatings on wood surfaces - Qualitative evaluation of scratch resistance of multilayer coatings on wood surfaces |
DOI : |
10.1007/s11998-014-9609-4 |
En ligne : |
https://link.springer.com/content/pdf/10.1007%2Fs11998-014-9609-4.pdf |
Format de la ressource électronique : |
Pdf |
Permalink : |
https://e-campus.itech.fr/pmb/opac_css/index.php?lvl=notice_display&id=22321 |
in JOURNAL OF COATINGS TECHNOLOGY AND RESEARCH > Vol. 11, N° 6 (11/2014) . - p. 993-1011
[article]
|