Titre : |
Effect of hot water and water-carrying agent on the properties of silane-water crosslinked linear low density polyethylene |
Type de document : |
texte imprimé |
Auteurs : |
T. Chen ; J. Wang ; P. Shi ; Q. Li ; C. Wu |
Année de publication : |
2013 |
Article en page(s) : |
p. 180-187 |
Note générale : |
Bibliogr. |
Langues : |
Anglais (eng) |
Catégories : |
Alun Eau Peroxyde de dicumyle Polyéthylène basse densité linéaire Polymères -- Propriétés mécaniques Polymères -- Propriétés thermiques Réticulation (polymérisation) Vinyltriméthoxysilane
|
Index. décimale : |
668.9 Polymères |
Résumé : |
The influence of hot water and the water-carrying agent aluminum potassium sulfate dodecahydrate (alum) on the mechanical and thermal properties of the silane-water crosslinked linear low density polyethylene (LLDPE) was investigated. LLDPE was melt-grafted with various content of vinyl trimethoxysilane (VTMS) using dicumyl peroxide (DCP) as initiator. The results show that the contribution of hot water to gel content is poor, about 2 to 16 %, compared with that of the silane grafted LLDPE. Is feasible to achieve silane-water crosslinking reaction with alum for self-crosslinked LLDPE; furthermore, the self-crosslinked LLDPE has lower crosslink density (m). It was found that alum could not only conduct silane-water crosslinking reaction effectively, but also improve the mechanical properties, especially the elongation behavior. The heat of fusion (DHm), the melting temperature (Tm), and the degree of crystallinity (Xc) of the hot water crosslinked LLDPE decreased with the advancement of VTMS. The Avrami exponent n of self-crosslinked sample was larger than that of hot water crosslinked sample. This means that the alum could contribute to the growth of crystallization. |
Note de contenu : |
- EXPERIMENTAL : Materials - Silane grafting and water crosslinking of LLDPE - Characterizations
- RESULTS AND DISCUSSION : Grafting analysis - Gel content and crosslink density - Mechanical properties - Thermal properties |
DOI : |
10.3139/217.2672 |
En ligne : |
https://drive.google.com/file/d/1OG_KmaUmczdSdbQK-aFwHggZaKVHpuB8/view?usp=drive [...] |
Format de la ressource électronique : |
Pdf |
Permalink : |
https://e-campus.itech.fr/pmb/opac_css/index.php?lvl=notice_display&id=18428 |
in INTERNATIONAL POLYMER PROCESSING > Vol. XXVIII, N° 2 (05/2013) . - p. 180-187