[article]
Titre : Lutter contre la corrosion : Protection par des composés triazoles de bronzes modernes et anciens recouverts de patine Type de document : texte imprimé Auteurs : Kamal Rahmouni, Auteur ; Hisasi Takenouti, Auteur Année de publication : 2009 Article en page(s) : p. 38-44 Note générale : Bibliogr. Langues : Français (fre) Catégories : Anticorrosifs
Antiquités (objets anciens) -- Conservation et restauration
Biens culturels -- Conservation et restauration
Bronze
Electrochimie
Microélectrodes
Monnaies antiques -- Conservation et restauration
Patine
TriazolesLes triazoles sont des composés organiques cycliques comportant un cycle à 5 atomes, comportant deux double liaisons et 3 atomes d'azote et donc de formule brute C2H3N3. Elles sont aromatiques et font partie des cycles excédentaires en électrons.
Selon la position des atomes d'azote, on distingue les 1,2,3-triazoles (appelées V-triazoles) et les 1,2,4-triazoles (appelées S-triazoles). (Wikipedia)Index. décimale : 541.37 Electrochimie et magnétochimie Résumé : Les objets archéologiques ou culturels en bronze sont nombreux et souvent exposés dans des musées ou dans les rues avec leur patine à la surface. Or ils subissent une dégradation significative due notamment à l'accroissement du niveau de pollution, alors que la patine protège partiellement le substrat. Pour exemple, nous présentons ici la protection de pièces de monnaie archéologiques marocaines en bronzes patinés par des dérivés de triazoles : benzotriazole, bi-triazole et amino-triazole. Sur l'une des pièces recouvertes de patine verte, la composition en éléments de la patine et celle du substrat ont été déterminées, puis l'effet inhibiteur de ces trois substances triazoliques sur une patine artificielle prélevée du substrat de bronze a été étudié. Enfin, le pouvoir inhibiteur a été évalué sur trois pièces de monnaie différentes. Il apparaît que parmi les trois composés examinés, l'amino-triazole est le plus intéressant pour cette utilisation. Note de contenu : - CONDITIONS EXPERIMENTALES : Pièces de monnaie archéologiques - Synthèse de patine sur une bronze moderne - MEB-EDS - Microspectroscopie Raman - Microélectrode à cavité - Solution d'essai de corrosion et inhibiteurs - Dispositif électronique
- RESULTATS ET DISCUSSION: Analyse par MEB-EDS - Analyse par spectroscopie Raman - Patine artificielle - Spectroscopie d'impédance - Protection des pièces de monnaie en bronzeEn ligne : https://new.societechimiquedefrance.fr/numero/lutter-contre-la-corrosion-protect [...] Format de la ressource électronique : Permalink : https://e-campus.itech.fr/pmb/opac_css/index.php?lvl=notice_display&id=16597
in L'ACTUALITE CHIMIQUE > N° 327-328 (02-03/2009) . - p. 38-44[article]Réservation
Réserver ce document
Exemplaires (1)
Code-barres Cote Support Localisation Section Disponibilité 011164 - Périodique Bibliothèque principale Documentaires Disponible Practical adhesion measurements of protective coatings on bronze by three-point bending test / Maëlenn Aufray in JOURNAL OF COATINGS TECHNOLOGY AND RESEARCH, Vol. 16, N° 5 (09/2019)
[article]
Titre : Practical adhesion measurements of protective coatings on bronze by three-point bending test Type de document : texte imprimé Auteurs : Maëlenn Aufray, Auteur ; Claudie Josse, Auteur ; Andrea Balbo, Auteur ; Cecilia Monticelli, Auteur ; Erika Svara Fabjan, Auteur ; Luka Skrlep, Auteur ; Tadeja Kosec, Auteur ; Nina Gartner, Auteur ; Carla Martini, Auteur ; Giulia Masi, Auteur ; Cristina Chiavari, Auteur ; Elena Bernardi, Auteur ; Maria Chiara Bignozzi, Auteur ; Luc Robbiola, Auteur ; Marija Babnik, Auteur ; Teja Korsic, Auteur ; Marko Kete, Auteur Année de publication : 2019 Article en page(s) : p. 1465-1477 Note générale : Bibliogr. Langues : Américain (ame) Catégories : Adhésion
Bronze
Essais dynamiques
Evaluation
Flexion trois points
Métaux -- Revêtements protecteurs
Objets d'art -- Conservation et restauration
Patine
Revêtements -- DétériorationIndex. décimale : 667.9 Revêtements et enduits Résumé : When attempting to sufficiently protect outdoor bronze monuments from corrosion, searches for an effective solution are usually based on coating applications which have a high anticorrosive efficiency. In order to correctly assess the level of protection provided by such coatings, adherence (practical adhesion) measurements need to be performed for the proper evaluation of the deterioration of coating systems with aging. Although a coupled study of adherence with aging would be of great interest, very few such studies are available. In this work, a methodological approach is proposed for the evaluation of coatings applied to metallic cultural heritage monuments of, based on the use of a three-point bending test. Adherence characterization of different protective coatings has been performed both on bare and on traditionally black-patinated bronze coupons (Cu–Sn alloy with 5.9 wt% Sn), which were used as basic model substrates. The investigated coatings were Incralac®, silane, sol–gel oxysilane, and a silane-modified polymethacrylate (an adhesion promoter for fluoropolymer). The results of measurements which were obtained before and after accelerated aging in concentrated acid rain made it possible to more easily differentiate between the various adherence levels of different coating systems. Coupled with adherence measurements, the results of systematic optical and SEM observation of the different failure morphologies are also presented. In the case of the coated bare alloy, adhesive failures were mainly observed. The silane (PropS-SH) coating showed the best adherence. In the case of the patinated bronze test specimens, only cohesive failures occurred. Adherence is directly related to the cohesion of the black patina rather than that of the applied coating. It was observed that aging reduces the level of the adherence. Note de contenu : - EXPERIMENTAL : Materials - The aging method - Practical adhesion measurements - Adhesive failure observation and surface characterization
- RESULTS AND DISCUSSION : Coated bare bronze (B) - Coated patinated bronze (P)DOI : 10.1007/s11998-019-00230-5 En ligne : https://link.springer.com/content/pdf/10.1007%2Fs11998-019-00230-5.pdf Format de la ressource électronique : Permalink : https://e-campus.itech.fr/pmb/opac_css/index.php?lvl=notice_display&id=33025
in JOURNAL OF COATINGS TECHNOLOGY AND RESEARCH > Vol. 16, N° 5 (09/2019) . - p. 1465-1477[article]Réservation
Réserver ce document
Exemplaires (1)
Code-barres Cote Support Localisation Section Disponibilité 21154 - Périodique Bibliothèque principale Documentaires Disponible Spectroscopie d'impédance électrochimique appliquée à l'étude de la corrosion / C. Gabrielli in MATERIAUX & TECHNIQUES, Vol. 95, Hors série (2007)
[article]
Titre : Spectroscopie d'impédance électrochimique appliquée à l'étude de la corrosion Type de document : texte imprimé Auteurs : C. Gabrielli, Auteur ; M. Keddam, Auteur ; H. Takenouti, Auteur Année de publication : 2008 Article en page(s) : p. 385-395 Note générale : Bibliogr. Langues : Français (fre) Catégories : Anticorrosifs
Antiquités (objets anciens) -- Conservation et restauration
Bronze
Corrosion électrochimique
Spectroscopie d'impédance électrochimiqueIndex. décimale : 620.11 Matériaux (propriétés, résistance) Résumé : Nous allons présenter différentes applications de la spectroscopie d'impédance électrochimique réalisées depuis 40 ans. Au début de cette longue histoire, l'emploi de signaux alternatifs était destiné à remplacer la méthode stationnaire dite de Stern et Geary, c'est-à -dire la mesure de la résistance de polarisation. Cependant, rapidement nous avons constaté que le spectre d'impédance contenait plusieurs informations sur les phénomènes se déroulant à l'interface métal | électrolyte. Ils se manifestent par une constante de temps propre à chaque processus, donc généralement distinguables par une analyse en fréquence. Après avoir présenté la différence majeure entre la méthode stationnaire et la méthode d'impédance dans l'étude de la corrosion à la fois en termes de compréhension des mécanismes et de prévision de sa vitesse, nous aborderons plusieurs applications de cette dernière méthode : la résistance d'électrolyte, l'effet protecteur d'inhibiteurs organiques et la protection de bronzes archéologiques recouverts de patine. DOI : http://dx.doi.org/10.1051/mattech:2008035 En ligne : http://www.mattech-journal.org/articles/mattech/pdf/2007/06/mt08030.pdf Format de la ressource électronique : Permalink : https://e-campus.itech.fr/pmb/opac_css/index.php?lvl=notice_display&id=26416
in MATERIAUX & TECHNIQUES > Vol. 95, Hors série (2007) . - p. 385-395[article]Réservation
Réserver ce document
Exemplaires (1)
Code-barres Cote Support Localisation Section Disponibilité 010923 - Périodique Bibliothèque principale Documentaires Disponible