Preparation and characterization of weather resistant silicone/acrylic resin coatings |
| Type de document : |
texte imprimé |
| Auteurs : |
Hong-Soo Park, Auteur ; S. R. Kim, Auteur ; H. J. Park, Auteur ; Y. C. Kwak, Auteur ; Hyun-Sik Hahm, Auteur ; S. K. Kim, Auteur |
| Année de publication : |
2003 |
| Article en page(s) : |
p. 55-64 |
| Note générale : |
Bibliogr. |
| Langues : |
Américain (ame) |
| Tags : |
'Etude expérimentale' Caractérisation 'Stabilité thermique' 'Propriété Couleur optique' Viscosité rhéologique' physique' Feuil 'Résistance intempérie' Polyméthacrylate de butyle' 'Polyméthacrylate méthyle' 'Copolymère Acrylate Silicones Préparation Liant Formulation Peinture 'Matériau revêtement' |
| Index. décimale : |
667.9 Revêtements et enduits |
| Résumé : |
Preparation and characterization of weather resistant silicone/acrylic resin coatings were conducted. In order to prepare these coatings, a silicone/acrylic resin (KLD) was first prepared by an addition polymerization reaction of monomers, including n-butyl acrylate, methyl methacrylate, n-butyl methacrylate, and 3-methacryloxypropyltrimethoxysilane (MPTS). In the preparation of the sillicone/acrylic resin, Tg of the acrylic copolymer was fixed at 40°C and the contents ofMPTS were varied to be 10, 20, and 30 wt%. The weather resistant silicone/acrylic resin coatings were then prepared by blending the synthesized silicone/ acrylic resin and TiO2. The viscosity of the synthesized resin decreased with the content of MPTS, whereas the thermal stability at high temperature increased. The prepared coatings exhibited excellent adhesion to various substrates, and various physical properties of the coatings were satisfactory. The weatherability of the coatings was tested three ways: outdoor exposure test, Weather-Ometer (WOM), and QUV accelerated weatherability tester (QUV). The gloss retention, yellowness index difference, color difference, and lightness index difference were improved at high MPTS concentration. The coatings containing 30 wt% MPTS have especially good weather properties. |
| Permalink : |
https://e-campus.itech.fr/pmb/opac_css/index.php?lvl=notice_display&id=5612 |
in JOURNAL OF COATINGS TECHNOLOGY (JCT) > Vol. 75, N° 936 (01/2003) . - p. 55-64
[article]
|
Aller sur edunet
Accueil
Preparation and characterization of weather resistant silicone/acrylic resin coatings in JOURNAL OF COATINGS TECHNOLOGY (JCT), Vol. 75, N° 936 (01/2003)