Synthesis of fully bio-based branched unsaturated polyester oligomers and UV curing coatings / Caixing Feng in JOURNAL OF COATINGS TECHNOLOGY AND RESEARCH, Vol. 20, N° 5 (09/2023)  

[article]  inJOURNAL OF COATINGS TECHNOLOGY AND RESEARCH > Vol. 20, N° 5 (09/2023) . - p. 1747-1758 Titre : Synthesis of fully bio-based branched unsaturated polyester oligomers and UV curing coatings Type de document : texte imprimé Auteurs : Caixing Feng, Auteur ; Haihong Ma, Auteur ; Fengmei Ren, Auteur ; Zhengfa Zhou, Auteur ; Weibing Xu, Auteur Année de publication : 2023 Article en page(s) : p. 1747-1758 Note générale : Bibliogr. Langues : Américain (ame) Catégories : Biopolymères Caractérisation Formulation (Génie chimique) Oligomères Polyesters insaturés Les résines de polyesters insaturés (UP) sont obtenues par polycondensation d’un ou de plusieurs diacides avec un ou plusieurs glycols, l’un, au moins, des constituants contenant une double liaison éthylénique susceptible de réagir ultérieurement sur un composé vinylique, acrylique ou allylique. Par le terme résine polyester, on désigne en fait la dissolution du prépolymère polyester insaturé dans un solvant copolymérisable, le plus utilisé étant le styrène. C’est sous cette forme liquide que les résines polyesters sont livrées aux transformateurs. Après addition de différents adjuvants, charges et renforts, divers procédés de transformation provoquent, sous l’action d’un système catalytique approprié, la copolymérisation finale de la résine en un objet thermodurcissable. Les polyesters insaturés sont d’un usage relativement ancien (1950), essentiellement dans le bâtiment (moulage au contact). Ils ont connu un renouveau important à partir de 1980, en particulier au niveau des formulations et de la fiabilité des procédés grâce au développement de technologies industrielles de moulage par injection et par compression dans l’industrie automobile. Polymères -- Synthèse Polymères ramifiés Revêtements -- Propriétés mécaniques Revêtements -- Propriétés thermiques Revêtements -- Séchage sous rayonnement ultraviolet Revêtements organiques Rugosité Surfaces -- Analyse Index. décimale : 667.9 Revêtements et enduits Résumé : In this paper, fully bio-based branched unsaturated polyester (BUPE) oligomers were synthesized by one-step solvent-free polycondensation using itaconic acid, isosorbide and glycerol as feedstocks. The branched structure was confirmed by Fourier-transform infrared spectroscopy (FTIR) and proton nuclear magnetic resonance spectroscopy (1H NMR). The effect of the branched structure on the properties of BUPE UV curing coatings was investigated. The results showed that the introduction of a glycerol branched structure was favorable for UV curing. The BUPE UV curing coatings based on the glycerol branched structure showed higher gel content and crosslink density, which enhanced the hardness, solvent resistance and mechanical properties of the coatings. In addition, the BUPE UV curing coatings possessed extremely low surface roughness, excellent heat resistance and light transmission properties. Note de contenu : - EXPERIMENT : Materials - Synthesis of branched unsaturated polyester (BUPE) oligomers - Preparation of BUPE UV curing coatings - Characterization - RESULTS AND DISCUSSION : Characterization of BUPE oligomers - Gel content and swelling ratio analysis - Mechanical properties analysis - Surface micromorphology and roughness analysis - Thermal property analysis - Coating performance analysis - Transparency analysis - Table 1 : Synthesis formula of BUPE oligomers - Table 2 : Data of BUPE oligomers obtained from 1H NMR, GPC and DSC - Table 3 : Data sheet of mechanical properties of BUPE UV curing films - Table 4 : TGA data - Table 5 : Performances of BUPE UV curing coatings and films DOI : https://doi.org/10.1007/s11998-023-00778-3 En ligne : https://link.springer.com/content/pdf/10.1007/s11998-023-00778-3.pdf?pdf=button% [...] Format de la ressource électronique : Pdf Permalink : https://e-campus.itech.fr/pmb/opac_css/index.php?lvl=notice_display&id=39985 [article]

Réservation

Réserver ce document

Exemplaires (1)

Code-barres	Cote	Support	Localisation	Section	Disponibilité
24242	-	Périodique	Bibliothèque principale	Documentaires	Disponible

---

1 (1 - 1 / 1)