Investigating the influence of nanosilica and fiber layer sequence on interlaminar shear strength in carbon-kevlar-epoxy polymer hybrid nanocomposite / Pranesh K Gopalakrishnamurthy in REVUE DES COMPOSITES ET DES MATERIAUX AVANCES, Vol. 33, N° 1 (02/2023)  

[article]  inREVUE DES COMPOSITES ET DES MATERIAUX AVANCES > Vol. 33, N° 1 (02/2023) . - p. 1-6 Titre : Investigating the influence of nanosilica and fiber layer sequence on interlaminar shear strength in carbon-kevlar-epoxy polymer hybrid nanocomposite Type de document : texte imprimé Auteurs : Pranesh K Gopalakrishnamurthy, Auteur ; Channabasavaraj Sandur, Auteur Année de publication : 2023 Article en page(s) : p. 1-6 Note générale : Bibliogr. Langues : Anglais (eng) Catégories : Cisaillement (mécanique) Composites -- Moulage par infusion sous vide Composites à fibres de carbone -- Propriétés mécaniques Epoxydes Nanoparticules Polyphénylènetéréphtalamide Le poly(p-phénylènetéréphtalamide) (PPD-T) est un polymère thermoplastique constitué de noyaux aromatiques séparés par des groupes amide. Il appartient à la famille des fibres d'aramides. Le poly-para-phénylène téréphtalamide a été découvert et commercialisé sous le nom déposé de Kevlar. Silice La silice est la forme naturelle du dioxyde de silicium (SiO2) qui entre dans la composition de nombreux minéraux. La silice existe à l'état libre sous différentes formes cristallines ou amorphes et à l'état combiné dans les silicates, les groupes SiO2 étant alors liés à d'autres atomes (Al : Aluminium, Fe : Fer, Mg : Magnésium, Ca : Calcium, Na : Sodium, K : Potassium...). Les silicates sont les constituants principaux du manteau et de l'écorce terrestre. La silice libre est également très abondante dans la nature, sous forme de quartz, de calcédoine et de terre de diatomée. La silice représente 60,6 % de la masse de la croûte terrestre continentale. Index. décimale : 668.4 Plastiques, vinyles Résumé : Present research work concentrated investigating the influence of adding nanosilica with epoxy matrix in varying weight percentages such as 0, 0.5, 1.0 and 1.5 on interlaminar shear strength in fiber reinforced polymer hybrid nanocomposite and fiber layer sequence. The polymer hybrid nanocomposite is having five carbon, four Kevlar layers (5C4K) and five Kevlar, four carbon (5K4C) layers of woven fibers. High speed shearing technique was used for the better dispersion of nanosilica with epoxy resin. Vacuum assisted resin infusion molding technique was used to fabricate the hybrid polymer nanocomposite laminates. Post curing was carried out effectively. Interlaminar shear strength test carried out according to ASTM D2344. The tested specimens show that 0.5 weight percentage of nanosilica with epoxy provides higher interlaminar shear strength than other weight percentage of nanosilica in both types of stacking sequences. The fiber layer sequence 5C4K shows better interlaminar shear strength as compared to 5K4C. Note de contenu : - Materials - Composite fabrication - Interlaminar shear strength - Table 1 : Fiber layer sequence (C- Carbon fiber and K-Kevlar fiber) - Table 2 : Weight percentage of nanosilica in polymer hybrid nanocomposite laminates DOI : https://doi.org/10.18280/rcma.330101 En ligne : https://iieta.org/download/file/fid/91629 Format de la ressource électronique : Pdf Permalink : https://e-campus.itech.fr/pmb/opac_css/index.php?lvl=notice_display&id=39259 [article]

Réservation

Réserver ce document

Exemplaires (1)

Code-barres	Cote	Support	Localisation	Section	Disponibilité
24132	-	Périodique	Bibliothèque principale	Documentaires	Disponible

---

1 (1 - 1 / 1)