Development of nano-magnesium oxide modified hybrid resin system for antimicrobial coating / Ujjal Kumar Dey in JOURNAL OF COATINGS TECHNOLOGY AND RESEARCH, Vol. 20, N° 1 (01/2023)  

[article]  inJOURNAL OF COATINGS TECHNOLOGY AND RESEARCH > Vol. 20, N° 1 (01/2023) . - p. 223-231 Titre : Development of nano-magnesium oxide modified hybrid resin system for antimicrobial coating Type de document : texte imprimé Auteurs : Ujjal Kumar Dey, Auteur ; Pradipta Sankar Maiti, Auteur ; Tapas Koley, Auteur ; Tapan Kumar Dhar, Auteur ; Tirthankar Jana, Auteur Année de publication : 2023 Article en page(s) : p. 223-231 Note générale : Bibliogr. Langues : Américain (ame) Catégories : Antimicrobiens Caractérisation Enrobage (technologie) Evaluation Mélanges (chimie) Nanoparticules Oxyde de magnésium L'oxyde de magnésium, communément appelé magnésie, a pour formule MgO et se présente sous la forme de poudre blanche très fortement basique absorbant l'eau et le dioxyde de carbone présents dans l'atmosphère. STRUCTURE : L'oxyde de magnésium est un cristal ionique. L'oxyde de magnésium a une structure comparable à celle du chlorure de sodium7. Cela se traduit par Un réseau d'anion oxygène formant une structure de type cubique à faces centrées Un réseau de cation magnésium occupant l'ensemble des sites octaèdriques. L'oxyde de magnésium est un matériau modèle des cristaux ioniques car la faible électronégativité du magnésium, et la forte électronégativité de l’oxygène font que la structure de l’oxyde de magnésium peut s’expliquer quasi uniquement grâce à des interactions entre des particules ponctuelles chargées 10. La surface de l'oxyde de magnésium la plus stable dans le vide est obtenue en réalisant une coupe selon le plan cristallographique (100). Les particules d'oxyde de magnésium produites par combustion du magnésium métallique présentent d'ailleurs une forme cubique révélatrice de la présence de ces plans. Néanmoins, en présence d'eau, la surface de l'oxyde de magnésium est couverte d'ions hydroxyles qui stabilisent les plans (111) PRODUCTION : La majeure partie de l'oxyde de magnésium est actuellement obtenue soit à partir de carbonate de magnésium MgCO3 qui constitue certains minéraux tels que la magnésite, soit à partir de chlorure de magnésium que l'on extrait de l'eau de mer ou de saumures souterraines. Polyacryliques Revêtements organiques Sol-gel, Procédé Index. décimale : 667.9 Revêtements et enduits Résumé : A novel organic-inorganic nanohybrid resin was synthesized through sol-gel process using nano magnesium oxide and specially designed acrylic resin. The uniqueness of this process is incorporation as well as dispersion of nano magnesium oxide into acrylic resin matrix where nano magnesium oxide is functional component. Magnesium oxide nanoparticles were successfully synthesized by sol-gel technique using magnesium nitrate as a precursor. Characterization of synthesized magnesium oxide nanoparticles and their distribution in acrylic resin matrix has been confirmed by spectroscopic, X-ray diffraction and SEM analysis. The coating based on such hybrid resin exhibited excellent anti-microbial activity. Such resin system has potential for application in antimicrobial coating. Note de contenu : - EXPERIMENTAL : Materials - Preparation of magnesium oxide nanoparticle - Synthesis of acrylic resin by solution polymerization - Synthesis of nano magnesium oxide-acrylic hybrid polymer - Preparation of nano magnesium oxide-acrylic resin mixture - CHARACTERIZATION : Physical characterization - FTIR spectroscopy Gel permeation chromatography - X-ray diffraction analysis - Differential scanning calorimetry analysis - Scanning electron microscopy analysis - Antimicrobial efficacy of the coating film as per JIS Z 2801 (2010) - RESULTS AND DISCUSSIONS : Physical properties of resin - FTIR spectroscopy - GPC analysis - XRD analysis - DSC study - FESEM analysis - Antimicrobial test results - Table 1 : Physical characteristics of acrylic and MgO modified acrylic resins - Table 2 : Evaluation of antibacterial activity (R) for each test bacterial strain after contact with MgO containing and STD antimicrobial coating samples DOI : https://doi.org/10.1007/s11998-022-https://doi.org/10.1007/s11998-022-00650-w En ligne : https://link.springer.com/content/pdf/10.1007/s11998-022-00650-w.pdf?pdf=button Format de la ressource électronique : Pdf Permalink : https://e-campus.itech.fr/pmb/opac_css/index.php?lvl=notice_display&id=38838 [article]

Réservation

Réserver ce document

Exemplaires (1)

Code-barres	Cote	Support	Localisation	Section	Disponibilité
23928	-	Périodique	Bibliothèque principale	Documentaires	Disponible

---

1 (1 - 1 / 1)