The effect of chromium on the chemical and physical properties of industrial sludge based geopolymer / Imad El Fellah in REVUE DES COMPOSITES ET DES MATERIAUX AVANCES, Vol. 32, N° 3 (06/2022)  

[article]  inREVUE DES COMPOSITES ET DES MATERIAUX AVANCES > Vol. 32, N° 3 (06/2022) . - p. 141-147 Titre : The effect of chromium on the chemical and physical properties of industrial sludge based geopolymer Type de document : texte imprimé Auteurs : Imad El Fellah, Auteur ; Rabie Fath Allah, Auteur ; Asmaa Fakih Lanjri, Auteur ; Mohammed Ammari, Auteur ; Laila Ben Allal, Auteur Année de publication : 2022 Article en page(s) : p. 141-147 Note générale : Bibliogr. Langues : Anglais (eng) Catégories : Boues résiduaires Boues thermales -- Analyse Caractérisation Chrome Géopolymères Les géopolymères sont la réciproque des polymères organiques. À la place de dérivés du pétrole et de la chaîne carbonée, on utilise de la matière minérale composée de silice et d’alumine. Les géopolymères sont basés sur des alumino-silicates désignés sous le terme poly(sialate), qui est une abréviation de poly(silico-oxo-aluminate) ou (-Si-O-Al-O-)n (soit n le degré de polymérisation). La structure chimique de la Figure 1 montre un géopolymère poly(sialate-siloxo) résultant d'une géosynthèse de poly(silisique) acide (SiO2)n et de potassium alumino-silicate, en milieu alcalin (KOH, NaOH). Dans cette structure, le groupement sialate (Si-O-Al-O-) est un agent de réticulation. On pense que le mécanisme de la synthèse géochimique se fait par l'intermédiaire d'oligomères (dimère, trimère) qui constituent les véritables groupements structuraux unitaires formant une structure macromoléculaire tridimensionnelle. Polymères -- Synthèse Résistance à la compression Index. décimale : 668.4 Plastiques, vinyles Résumé : This paper investigates the immobilization of chromium in the industrial sludge-based geopolymer. Mechanical, physical and microstructure properties were used to characterize different samples. The results show that lower heavy metals addition has less effect on the compressive strength. However, excessive addition of Cr(VI) (1.5 and 3%) causes a deterioration of geopolymer matrix with a significant drop of the compressive strength. The compressive strength shows that the use of sodium hydroxide as an alkaline activator is not suitable for chromium immobilization. The use of 1.5 and 3% amount of chromium increases the conductivity of leachates, which explains a change in the microstructure of materials. This is in agreement with the results of compressive strength. XRD patterns of all samples show an amorphous structure with less effect of chromium on the crystalline phases. SEM of the reference sample demonstrates a dense structure of binder. However, the porosity of the matrix increases with the addition of 3% Cr(VI). Note de contenu : - MATERIALS AND METHODS : Materials - Synthesis of geopolymers - Compressive strength - Conductivity - Characterization - RESULTS AND DISCUSSION : Compressive strength - The effect of chromium on the conductivity of leachetes - X-ray diffraction analysis (XRD) Scanning electron microscope (SEM) and energy-dispersive X-ray spectroscopy (EDS) - Table 1 : Chemical composition of industrial sludge determined by X-ray fluorescence - Table 2 : The mix proportions used for the preparation of geopolymer samples DOI : https://doi.org/10.18280/rcma.320305 En ligne : https://www.iieta.org/download/file/fid/77317 Format de la ressource électronique : Pdf Permalink : https://e-campus.itech.fr/pmb/opac_css/index.php?lvl=notice_display&id=38206 [article]

Réservation

Réserver ce document

Exemplaires (1)

Code-barres	Cote	Support	Localisation	Section	Disponibilité
23830	-	Périodique	Bibliothèque principale	Documentaires	Disponible

---

1 (1 - 1 / 1)