Experimental investigation on tensile properties of carbon fabric-glass fabric-kevlar fabric-epoxy hybrid composite laminates / Samer Al Khaddour in REVUE DES COMPOSITES ET DES MATERIAUX AVANCES, Vol. 31, N° 3 (06/2021)  

[article]  inREVUE DES COMPOSITES ET DES MATERIAUX AVANCES > Vol. 31, N° 3 (06/2021) . - p. 145-151 Titre : Experimental investigation on tensile properties of carbon fabric-glass fabric-kevlar fabric-epoxy hybrid composite laminates Type de document : texte imprimé Auteurs : Samer Al Khaddour, Auteur ; Mohamad Barkat Ibrahim, Auteur Année de publication : 2021 Article en page(s) : p. 145-151 Note générale : Bibliogr. Langues : Français (fre) Catégories : Caractérisation Composites à fibres de carbone -- Propriétés mécaniques Composites à fibres de verre -- Propriétés mécaniques Epoxydes Essais dynamiques Matériaux hybrides -- Propriétés mécaniques Polyphénylènetéréphtalamide Le poly(p-phénylènetéréphtalamide) (PPD-T) est un polymère thermoplastique constitué de noyaux aromatiques séparés par des groupes amide. Il appartient à la famille des fibres d'aramides. Le poly-para-phénylène téréphtalamide a été découvert et commercialisé sous le nom déposé de Kevlar. Stratifiés -- Propriétés mécaniques Tissés Traction (mécanique) Index. décimale : 668.4 Plastiques, vinyles Résumé : In this paper, composite and hybrid composite materials were prepared using the hand lay-up method, with carbon, glass, and Kevlar fabrics as the reinforcing materials and epoxy as a matrix. The tensile test was performed to determine the optimal ratio of epoxy resin in carbon fabric/epoxy, glass fabric/epoxy, and Kevlar fabric/epoxy composites in terms of tensile properties. It was found that the optimal ratio of epoxy in terms of tensile properties to impregnate the used Kevlar fabric, glass fabric, and carbon fabric was around 45%wt, 3%wt, and 30 %wt, respectively. The effect of fabric content and stacking sequences, with a fixed epoxy content, on the hybrid composites’ tensile properties were also investigated. The tensile properties of the prepared composites were compared to determine the most favorable preparation conditions for obtaining a hybrid laminate that has high tensile properties and is suitable for a wide range of applications at a low cost. Note de contenu : - MATERIALS AND METHODS : Materials - Preparation of composites and specimens - Mechanical characterization - RESULTS AND DISCUSSION : Fabrics/epoxy non-hybrid composites - Kevlar-Carbon-epoxy30% hybrid composites - Glass-Carbon-epoxy30% hybrid composites - Glass-Kevlar-epoxy30% hybrid composites - Carbon-Glass-Kevlar-epoxy30% hybrid composites - Table 1 : Codes of composites - Table 2 : Tensile test results of hybrid and non-hybrid composites - Table 3 : Tensile results of hybrid composites that contain three fabrics types DOI : https://doi.org/10.18280/rcma.310305 En ligne : https://www.iieta.org/download/file/fid/56444 Format de la ressource électronique : Pdf Permalink : https://e-campus.itech.fr/pmb/opac_css/index.php?lvl=notice_display&id=37669 [article]

Exemplaires

Code-barres	Cote	Support	Localisation	Section	Disponibilité
aucun exemplaire

---

1 (1 - 1 / 1)