Influence of alkali treatment and dune sand content on the properties of date palm fiber reinforced unsaturated polyester hybrid composites / Yazid Meftah in REVUE DES COMPOSITES ET DES MATERIAUX AVANCES, Vol. 30, N° 3-4 (08/2020)  

[article]  inREVUE DES COMPOSITES ET DES MATERIAUX AVANCES > Vol. 30, N° 3-4 (08/2020) . - p. 161-167 Titre : Influence of alkali treatment and dune sand content on the properties of date palm fiber reinforced unsaturated polyester hybrid composites Type de document : texte imprimé Auteurs : Yazid Meftah, Auteur ; Masoud Tayefi, Auteur ; Fatma Fellouh, Auteur ; Houria Chouieur, Auteur ; Samira Maou, Auteur ; Ahmed Meghezzi, Auteur Année de publication : 2020 Article en page(s) : p. 161-167 Note générale : Bibliogr. Langues : Français (fre) Catégories : Caractérisation Composites -- Propriétés mécaniques Composites -- Propriétés physiques Composites -- Propriétés thermiques Composites à fibres végétales Fibres de palmier dattier Humidité -- Absorption:Eau -- Absorption Matériaux hybrides Polyesters insaturés Les résines de polyesters insaturés (UP) sont obtenues par polycondensation d’un ou de plusieurs diacides avec un ou plusieurs glycols, l’un, au moins, des constituants contenant une double liaison éthylénique susceptible de réagir ultérieurement sur un composé vinylique, acrylique ou allylique. Par le terme résine polyester, on désigne en fait la dissolution du prépolymère polyester insaturé dans un solvant copolymérisable, le plus utilisé étant le styrène. C’est sous cette forme liquide que les résines polyesters sont livrées aux transformateurs. Après addition de différents adjuvants, charges et renforts, divers procédés de transformation provoquent, sous l’action d’un système catalytique approprié, la copolymérisation finale de la résine en un objet thermodurcissable. Les polyesters insaturés sont d’un usage relativement ancien (1950), essentiellement dans le bâtiment (moulage au contact). Ils ont connu un renouveau important à partir de 1980, en particulier au niveau des formulations et de la fiabilité des procédés grâce au développement de technologies industrielles de moulage par injection et par compression dans l’industrie automobile. Sable Thermogravimétrie Traîtements de surface Index. décimale : 668.4 Plastiques, vinyles Résumé : The effects of alkali treatment and dune sand (DS) addition on the mechanical, morphological, thermal and water absorption behavior of date palm fiber (DPF) reinforced unsaturated polyester (UP) composites were investigated. The composites were synthesized by hand lay-up method with 10, 20, and 30 wt% of both treated and untreated date palm fiber (TDPF/DPF). Furthermore, composites having 10, 20 and 30 wt% of untreated date palm fiber and dune sand (both of them were in equal wt%) were also fabricated. Alkali treatment improved the tensile strength, tensile modulus, flexural strength and flexural modulus of the resulting composites. Scanning electron microscopy (SEM) revealed the better interfacial interaction of treated date palm fibers/UP composites. Thermogravimetric analysis (TGA) showed that thermal stability, and degradation temperature of treated DPF composites were best over the untreated DPF composites. Water absorption test indicated the decreasing of hydrophilic character of the filler after treatment with sodium hydroxide (NaOH). Overall analysis represented that satisfactorily improved physical properties of UP for various engineered and hi-tech applications were obtained with 10 wt% fillers loading (5 wt% date palm fiber and 5 wt% dune sand particles). Note de contenu : - MATERIALS AND METHODS : Materials - Surface modification of date palm fibers with NaOH - Fabrication of composites - Characterization - RESULTS AND DISCUSSION : Mechanical properties - Morphological properties - Thermogravimetric (TGA) and differential thermogravimetric (DTGA) analysis - Water absorption - Table 1 : Physical characteristics of dune sand - Table 2 : Chemical composition of leaf date palm fibers - Table 3 : Thermal properties of different UP based composites DOI : https://doi.org/10.18280/rcma.303-406 En ligne : https://www.iieta.org/download/file/fid/39667 Format de la ressource électronique : Pdf Permalink : https://e-campus.itech.fr/pmb/opac_css/index.php?lvl=notice_display&id=37641 [article]

Exemplaires

Code-barres	Cote	Support	Localisation	Section	Disponibilité
aucun exemplaire

---

1 (1 - 1 / 1)