Preparation and properties of thermally expandable microspheres for foam coating / Guodong Huang in JOURNAL OF THE AMERICAN LEATHER CHEMISTS ASSOCIATION (JALCA), Vol. CXVI, N° 7 (07/2021)  

[article]  inJOURNAL OF THE AMERICAN LEATHER CHEMISTS ASSOCIATION (JALCA) > Vol. CXVI, N° 7 (07/2021) . - p. 249-259 Titre : Preparation and properties of thermally expandable microspheres for foam coating Type de document : texte imprimé Auteurs : Guodong Huang, Auteur ; Zhixian Lin, Auteur ; Haojun Fan, Auteur ; Jun Xiang, Auteur ; Chong Zheng, Auteur ; Zhiqing Luo, Auteur Année de publication : 2021 Article en page(s) : p. 249-259 Note générale : Bibliogr. Langues : Américain (ame) Catégories : Croûte (cuir) On entend par "cuir en croûte" des cuirs ayant subi les opérations jusqu'au tannage, à l'exclusion de toute opération de corroyage ou de finissage, mais qui, par opposition aux wet-blue ont été séchés. Cuirs et peaux -- Finition Fleur du cuir Formulation (Génie chimique) Microsphères Moussants Mousses plastiques Polyacétate de vinyle Polyacrylonitrile Polymères expansés Polyméthacrylate de méthyle Le poly(méthacrylate de méthyle) (souvent abrégé en PMMA, de l'anglais Poly(methyl methacrylate)) est un polymère thermoplastique transparent obtenu par polyaddition dont le monomère est le méthacrylate de méthyle (MMA). Ce polymère est plus connu sous son premier nom commercial de Plexiglas (nom déposé), même si le leader global du PMMA est Altuglas International9 du groupe Arkema, sous le nom commercial Altuglas. Il est également vendu sous les noms commerciaux Lucite, Crystalite, Perspex ou Nudec. Résistance chimique Réticulation (polymérisation) Revêtements organiques Index. décimale : 675 Technologie du cuir et de la fourrure Résumé : A type of thermally expandable microspheres (TEMs) for foam coating was prepared by suspension polymerization with acrylonitrile (AN), methyl methacrylate (MMA), vinyl acetate (VAC) as shell polymer monomers and i-pentane as core foaming agent. The effects of an aqueous additive (Sodium Chloride, NaCl) on the size and distribution of TEMs, and the effects of crosslinking degree, i-pentane dosage and monomer mass ratio on the expansion property, expansion temperature and solvent-resistance of TEMs were investigated. The results showed that when the dosage of NaCl was close to the saturation solubility (30%), the dosage of crosslinking agent and alkane were about 0.09% and 7.4%, and the mass ratio of AN/MMA/VAC w rm distribution and good solvent resistance, the expansion diameter ratio was 5 times under 110~120 C, which meets the application requirements for foam coating of leather or synthetic leather. Note de contenu : - MATERIALS AND METHODS : Experimental materials - Preparation of TEMs - Preparation of foaming coating - Finishing of split leather and damaged grain leather - CHARACTERISTICS OF TEMS : Determination of particle size and distribution - Observation on surface morphology - Determination of expansion property and temperature - RESULTS AND DISCUSSION : Structure design of TEMs - Effect of NaCl concentration on the size and distribution of TEMs - Effect of crosslinking degree on the expansion property and temperature of TEMs - Effect of dosage of alkane on expansion property and temperature of TEMs - Effect of monomer mass ratio on expansion property, temperature and solvent resistance of TEMs - Morphology of split leather foam coating - Matting and mending effect of foaming coating - Table 1 : The basic formula for preparing TEMs - Table 2 : Foaming properties and foaming temperature of TEMS with different content of EGDMA - Table 3 : Effect of foaming agent dosage on the expansion property and foaming temperature of thermally expanded microspheres - Table 4 : Effect of monomer ratio on the expansion property and expansion temperature of thermally expanded microspheres DOI : https://doi.org/10.34314/jalca.v116i7.4336 En ligne : https://drive.google.com/file/d/1i1pJAJAQnAwYRmogNbezp7Ho-pyNhhl1/view?usp=drive [...] Format de la ressource électronique : Pdf Permalink : https://e-campus.itech.fr/pmb/opac_css/index.php?lvl=notice_display&id=36082 [article]

Réservation

Réserver ce document

Exemplaires (1)

Code-barres	Cote	Support	Localisation	Section	Disponibilité
22869	-	Périodique	Bibliothèque principale	Documentaires	Disponible

---

1 (1 - 1 / 1)