Scalable coating process of AgNPs-silicone on cotton fabric for developing hydrophobic and antimicrobial properties / Md. Touhidul Islam in JOURNAL OF COATINGS TECHNOLOGY AND RESEARCH, Vol. 18, N° 3 (05/2021)  

[article]  inJOURNAL OF COATINGS TECHNOLOGY AND RESEARCH > Vol. 18, N° 3 (05/2021) . - p. 887-898 Titre : Scalable coating process of AgNPs-silicone on cotton fabric for developing hydrophobic and antimicrobial properties Type de document : texte imprimé Auteurs : Md. Touhidul Islam, Auteur ; Md. Abdullah Al. Mamun, Auteur ; Md. Tusher Hasan, Auteur ; Hasan Shahariar, Auteur Année de publication : 2021 Article en page(s) : p. 887-898 Note générale : Bibliogr. Langues : Américain (ame) Catégories : Antibactériens Argent Caractérisation Coton Le coton est une fibre végétale qui entoure les graines des cotonniers "véritables"(Gossypium sp.), un arbuste de la famille des Malvacées. Cette fibre est généralement transformée en fil qui est tissé pour fabriquer des tissus. Le coton est la plus importante des fibres naturelles produites dans le monde. Depuis le XIXe siècle, il constitue, grâce aux progrès de l'industrialisation et de l'agronomie, la première fibre textile du monde (près de la moitié de la consommation mondiale de fibres textiles). Enduction textile Hydrophobie Mouillage (chimie des surfaces) Nanoparticules Revêtements Silicones Les silicones, ou polysiloxanes, sont des composés inorganiques formés d'une chaine silicium-oxygène (...-Si-O-Si-O-Si-O-...) sur laquelle des groupes se fixent, sur les atomes de silicium. Certains groupes organiques peuvent être utilisés pour relier entre elles plusieurs de ces chaines (...-Si-O-...). Le type le plus courant est le poly(diméthylsiloxane) linéaire ou PDMS. Le second groupe en importance de matériaux en silicone est celui des résines de silicone, formées par des oligosiloxanes ramifiés ou en forme de cage (wiki). Tests d'efficacité Textiles et tissus Index. décimale : 667.9 Revêtements et enduits Résumé : Developing a scalable and cost-effective coating process is critical to manufacturing cotton-based hydrophobic antimicrobial fabric for various commercial applications. This paper describes a scalable, cost-effective coating process that is compatible with the existing industrial finishing processes of fabrics. In this process, the fabric is continuously dipped in water-based silver salt and the reducing agent solution to impart silver particles on the fiber surface to produce different coated samples. The process is tuned to minimize process cost and material cost and maximize the antimicrobial effectiveness and durability of the fabric. This paper also introduces an easy protective coating technique with silicone binder of the antimicrobial fabric that improves the durability and hydrophobicity of the antimicrobial fabric without sacrificing the comfort properties of textile fabrics. In the presence of silicone binder, the samples show significant antibacterial effectiveness against two microorganisms, gram-positive Staphylococcus aureus and gram-negative Escherichia coli bacteria. Qualitative assessment is carried out to evaluate the antimicrobial properties of the silicone encapsulated silver particles-coated fabrics. Moreover, among the silver-coated fabrics of different cycles, silver nanoparticles (AgNPs) are deposited in the 1 cycle of silver-coated fabric and the average particle size deposited onto the fiber surface is 65.52 ± 2.71 nm. After silicone encapsulation, among all encapsulated samples, 1 cycle of silver-coated silicone encapsulated sample shows the best result in terms of antimicrobial efficacy where silicone encapsulated 1 cycle silver-coated sample shows around the zone of inhibition 0.53 and 0.25 mm and encapsulated 2 cycles silver-coated sample shows the zone of inhibition 0.14 and 0.06 mm for S. aureus and E. coli, respectively. Coated fabrics with and without silicone encapsulation are characterized by scanning electron microscopy and energy-dispersive X-ray spectroscopy. Note de contenu : - EXPERIMENTAL PROCESS : Materials - Functional coating procedure - Weight-gain % - Hydrophobicity test - Scanning electron microscopy (SEM) and energy-dispersive X-ray spectroscopy (EDS) analysis - Antimicrobial effectiveness assessment - RESULTS AND DISCUSSION : Surface topography of the samples and morphology of the silver particles - Surface wetting behavior - Antimicrobial effectiveness - - Table 1 : N° of samples which will be considered for further experiments DOI : https://doi.org/10.1007/s11998-020-00451-z En ligne : https://link.springer.com/content/pdf/10.1007/s11998-020-00451-z.pdf Format de la ressource électronique : Pdf Permalink : https://e-campus.itech.fr/pmb/opac_css/index.php?lvl=notice_display&id=35937 [article]

Réservation

Réserver ce document

Exemplaires (1)

Code-barres	Cote	Support	Localisation	Section	Disponibilité
22785	-	Périodique	Bibliothèque principale	Documentaires	Disponible

---

1 (1 - 1 / 1)