Characterization, coating and biological evaluation of polyol esters rosin derivatives as coating films / A. A. Soliman in JOURNAL OF COATINGS TECHNOLOGY AND RESEARCH, Vol. 18, N° 2 (03/2021)  

[article]  inJOURNAL OF COATINGS TECHNOLOGY AND RESEARCH > Vol. 18, N° 2 (03/2021) . - p. 373-381 Titre : Characterization, coating and biological evaluation of polyol esters rosin derivatives as coating films Type de document : texte imprimé Auteurs : A. A. Soliman, Auteur ; M. M. Elsawy, Auteur ; N. A. Alian, Auteur ; N. O. Shaker, Auteur Année de publication : 2021 Article en page(s) : p. 373-381 Note générale : Bibliogr. Langues : Américain (ame) Catégories : Antibactériens Caractérisation Colophane La colophane est le résidu solide obtenu après distillation de la térébenthine, oléorésine (appelée aussi gemme), substance récoltée à partir des arbres résineux et en particulier les pins (le genre Pinus) par une opération que l'on appelle le gemmage. La colophane est solide et cassante à température ambiante. Sa couleur va du jaune très clair au quasi noir en fonction essentiellement de la conduite de la distillation, la couleur ou grade est défini par une échelle de lettre allant de D pour le plus foncé à X pour le plus clair. La colophane ne fond pas mais se ramollit avec la chaleur, son point de ramollissement se situant autour de 70 °C. Cette résine a les propriétés de coller et d'imperméabiliser. Elle fait partie des liants utilisés dans les antifoulings. La colophane est composée à 90% d’un mélange d’acides organiques de la famille des diterpènes appelés acides résiniques, qui répondent à la formule brute C20H30O2. Ces acides résiniques sont des isomères. La proportion des différents acides résiniques dans la colophane est variable suivant l’espèce de pin à partir de laquelle la colophane a été obtenue. Certains acides ne sont présents que chez certaines espèces (et leur sont donc caractéristiques). La colophane (ou « rosine ») a de nombreux usages. On la trouve notamment dans les peintures antifouling où elle se substitue au tributylétain interdit. C'est un irritant et un allergisant pour la peau et les voies respiratoires, sous forme pure ou par ses produits de dégradation. Enrobage (technologie) Esters Polyols Revêtements -- Analyse Revêtements -- Propriétés chimiques Revêtements -- Propriétés mécaniques Revêtements organiques Index. décimale : 667.9 Revêtements et enduits Résumé : Polyol esters materials, which have been developed from ethylene glycol, glycerol, pentaerythritol and sorbitol with rosin, were investigated for their formed films and coating properties. Films were dried and characterized for chemical and mechanical resistances. Their films were highly resistant to water, solvents (acetone, toluene and methanol), and acids (10% hydrochloric acid and 20% sulfuric acid) and poorly resistant to alkali (10% sodium hydroxide) as well as adhesion, tensile strength, elongation test, modulus of elasticity, pinhole test and scratching and flexibility tests. Incorporation of ethylene glycol, glycerol, pentaerythritol and sorbitol with rosin was done to achieve good mechanical characteristics and high chemical resistance to these films. The prepared compounds were tested for antibacterial activity against Trametes versicolor and Gloeophyllum trabeum. Note de contenu : - MATERIALS AND METHODS - CHARACTERIZATION OF BIOMATERIALS : Free film preparation and characterization - Bioactivity of rosin derivatives - RESULTS AND DISCUSSION : Synthesis of polyol esters of maleic rosin (EGMR, GMR, PMR, SMR) - Physicochemical properties - Evaluation of film properties - - Table 1 : Characterization of biomaterials derivatives - Table 2 : Drying time characteristic data of biomaterials - Table 3 : Water resistance data of biomaterials - Table 4 : Acid resistance of 10% HCl of biomaterials - Table 5 : Acid resistance of 20% H2SO4 of biomaterials - Table 6 : Alkali resistance of 10% NaOH of biomaterials - Table 7 : Acetone resistance of biomaterials - Table 8 : Toluene resistance of biomaterials - Table 9 : Methanol resistance of biomaterials - Table 10 : Mechanical characteristics of stoved films of biomaterials - Table 11 : Average diameter of inhibition zone of control of biomaterials against Trametes versicolor and Gloeophyllum trabeum in 0.025 mm DOI : https://doi.org/10.1007/s11998-020-00408-2 En ligne : https://link.springer.com/content/pdf/10.1007/s11998-020-00408-2.pdf Format de la ressource électronique : Pdf Permalink : https://e-campus.itech.fr/pmb/opac_css/index.php?lvl=notice_display&id=35601 [article]

Réservation

Réserver ce document

Exemplaires (1)

Code-barres	Cote	Support	Localisation	Section	Disponibilité
22701	-	Périodique	Bibliothèque principale	Documentaires	Disponible

---

1 (1 - 1 / 1)