Specific crosslinking effects of poly(epichlorohydrin)-triol on urethane polymer matrix of castor seel oil-based coatings / T. O. Siyanbola in JOURNAL OF COATINGS TECHNOLOGY AND RESEARCH, Vol. 18, N° 1 (01/2021)  

[article]  inJOURNAL OF COATINGS TECHNOLOGY AND RESEARCH > Vol. 18, N° 1 (01/2021) . - p. 129-141 Titre : Specific crosslinking effects of poly(epichlorohydrin)-triol on urethane polymer matrix of castor seel oil-based coatings Type de document : texte imprimé Auteurs : T. O. Siyanbola, Auteur ; R. Enishetty, Auteur ; R. Kumar, Auteur ; O. O. james, Auteur ; G. I. Olasehinde, Auteur ; S. Kaki, Auteur ; R. Nayaran, Auteur ; K. V. S. N. Raju, Auteur Année de publication : 2021 Article en page(s) : p. 129-141 Note générale : Bibliogr. Langues : Américain (ame) Catégories : Acier L'acier est un alliage métallique utilisé dans les domaines de la construction métallique et de la construction mécanique. L'acier est constitué d'au moins deux éléments, le fer, très majoritaire, et le carbone, dans des proportions comprises entre 0,02 % et 2 % en masse1. C'est essentiellement la teneur en carbone qui confère à l'alliage les propriétés du métal qu'on appelle "acier". Il existe d’autres métaux à base de fer qui ne sont pas des aciers comme les fontes et les ferronickels par exemple. Adhésion Antibactériens Anticorrosion Caractérisation Huile de ricin et constituants Hydrophobie Métaux -- Revêtements protecteurs Polyépichlorhydrine Polyuréthanes Résistance chimique Revêtements -- Propriétés mécaniques Revêtements organiques Stabilité thermique Index. décimale : 667.9 Revêtements et enduits Résumé : The contributions of castor seed oil (CSO) as a useful, nontoxic, and sustainable base material for coating systems cannot be overemphasized. This paper took advantage of the predominant fatty acid composition in CSO (i.e., ricinoleic acid). It blended a synthesized crosslinker, poly(epichlorohydrin-triol) (PECH-triol), in percentages within its polymeric matrix. Physicochemical and spectroscopic (FTIR, 1H-NMR, and 13C-NMR) examinations were carried out on the polyols. Thermal stability, hydrophobicity, anticorrosion, mechanical, and antibacterial properties of the prepared polyurethane (PU) coatings were examined. The 20% PECH-triol–CSO-PU film having its TON and TEND at 230.5 and 511.0°C, respectively, showed improved thermal stability when compared with the pristine film (CSO-PU). The derivative of TGA reveals a three-stage degradation step. Hydrophobicity was seen to increase from 73.3° to 92.2°, a reflection of the crosslinking effect of PECH-triol within the urethane matrix. The improved adhesion of 20% PECH-triol–CSO-PU coating on mild steel gave a better chemical resistance. Note de contenu : - EXPERIMENTAL : Materials - Preparation - Characterization - RESULTS AND DISCUSSION : Physicochemical properties CSO and PECH-triol - Flow curve analysis and molecular weight of CSO and PECH-triol - Spectroscopic analyses of synthesized compounds - Thermal analysis of PU films - Contact angle - Electrochemical analysis - UTM analysis of coating films - Antimicrobial study of the films - Chemical resistance and drying behavior of coating films - Table 1 : Physicochemical properties of CSO and PECH-triol - Table 2 : Thermal behavior data of polyurethane films - Table 3 : Corrosion parameters of coated and uncoated mild steel in 3.5% NaCl - Table 4 : UTM analysis of polyurethane coating films - Table 5 : Antimicrobial activities of pristine and blended polyurethanes - Table 6 : Drying time and chemical resistance of resins DOI : https://doi.org/10.1007/s11998-020-00387-4 En ligne : https://link.springer.com/content/pdf/10.1007/s11998-020-00387-4.pdf Format de la ressource électronique : Pdf Permalink : https://e-campus.itech.fr/pmb/opac_css/index.php?lvl=notice_display&id=35357 [article]

Réservation

Réserver ce document

Exemplaires (1)

Code-barres	Cote	Support	Localisation	Section	Disponibilité
22605	-	Périodique	Bibliothèque principale	Documentaires	Disponible

---

1 (1 - 1 / 1)