The effects of nanosilica and nanoclay particles inclusions on mode II delamination, thermal and water absorption of intraply woven carbon/aramid hybrid composites / Mehmet Bulut in INTERNATIONAL POLYMER PROCESSING, Vol. XXXV, N° 4 (08/2020)  

[article]  inINTERNATIONAL POLYMER PROCESSING > Vol. XXXV, N° 4 (08/2020) . - p. 367-375 Titre : The effects of nanosilica and nanoclay particles inclusions on mode II delamination, thermal and water absorption of intraply woven carbon/aramid hybrid composites Type de document : texte imprimé Auteurs : Mehmet Bulut, Auteur ; M. Alsaadi, Auteur ; A. Erklig, Auteur Année de publication : 2020 Article en page(s) : p. 367-375 Note générale : Bibliogr. Langues : Anglais (eng) Catégories : Composites -- Délaminage Composites à fibres Composites à fibres -- Propriétés thermiques Essais (technologie) Fibre aramide Fibres de carbone Humidité -- Absorption:Eau -- Absorption Nanoparticules Silice La silice est la forme naturelle du dioxyde de silicium (SiO2) qui entre dans la composition de nombreux minéraux. La silice existe à l'état libre sous différentes formes cristallines ou amorphes et à l'état combiné dans les silicates, les groupes SiO2 étant alors liés à d'autres atomes (Al : Aluminium, Fe : Fer, Mg : Magnésium, Ca : Calcium, Na : Sodium, K : Potassium...). Les silicates sont les constituants principaux du manteau et de l'écorce terrestre. La silice libre est également très abondante dans la nature, sous forme de quartz, de calcédoine et de terre de diatomée. La silice représente 60,6 % de la masse de la croûte terrestre continentale. Tissés Tissus sergés La serge est l'une des trois armures principales de tissage. Ainsi, la serge désigne l'ensemble des textiles élaborés par ce type de tissage qui se caractérisent par la présence de côtes obliques sur l'endroit et sont unis sur l'envers. Elle peut être à effet chaîne ou trame. Le fil de trame passe sous un, puis sur trois autres fils de chaîne en décalant d'un fil à chaque passage d'où l'effet d'oblique sur l'endroit. Index. décimale : 668.4 Plastiques, vinyles Résumé : The effects of nanosilica (NS) and nanoclay (NC) particle inclusions on mode II delamination and thermal properties as well as water absorption capability of carbon/aramid fiber reinforced hybrid composites (CAFRE) were experimentally investigated at different nanoparticle contents. NS and NC particles modified CAFRE samples were reinforced with intraply woven and twill weave of carbon and aramid fibers, and were manufactured by using hot mold press assisted with hand-layup method. Various thermal properties such as thermal conductivity, thermal diffusivity, and specific heat capacity were experimentally measured with respect to NS and NC particle weight contents according to ISO-22007 standard. In addition, the water absorption test was performed according to ASTM D570-98 standard. Results from this study showed that addition of NS and NC particles improved mode II delamination toughness of CAFRE composites at 1.5 wt% and 2 wt% of NS and NC particle contents, respectively. Water absorption capacity of the CAFRE samples was increased as increasing NS and NC weigh contents while thermal tests showed that thermal diffusivity values increased, and specific heat decreased with increasing both NC and NS particle weight contents. Note de contenu : - MATERIALS AND METHODS : Materials production - Preparation of test samples - Mode II fracture tests with notched test samples - Water absorption tests - Thermal properties - RESULTS AND DISCUSSIONS : Mechanism of mode II interlaminar toughness - Water abrosption test results - Thermal test results DOI : https://doi.org/10.3139/217.3940 En ligne : https://drive.google.com/file/d/1n4A5CrXu_gef1KNbn9J5yctmgshGQhTc/view?usp=drive [...] Format de la ressource électronique : Pdf Permalink : https://e-campus.itech.fr/pmb/opac_css/index.php?lvl=notice_display&id=34695 [article]

Réservation

Réserver ce document

Exemplaires (1)

Code-barres	Cote	Support	Localisation	Section	Disponibilité
21877	-	Périodique	Bibliothèque principale	Documentaires	Disponible

---

1 (1 - 1 / 1)