| Titre : |
Morphological changes in exterior surface coatings after exposure to cyclic water submersion and ultraviolet exposure |
| Type de document : |
texte imprimé |
| Auteurs : |
Armin B. Burghart, Auteur ; Sridhar G. Lyer, Auteur ; William J. Rosano, Auteur |
| Année de publication : |
2020 |
| Article en page(s) : |
p. 28-35 |
| Note générale : |
Bibliogr. |
| Langues : |
Américain (ame) |
| Catégories : |
Immersion
Morphologie (matériaux)
Revêtements -- Analyse:Peinture -- Analyse
Revêtements -- Défauts:Peinture -- Défauts
Revêtements -- Effets du rayonnement ultraviolet:Peinture -- Effets du rayonnement ultraviolet
Revêtements organiques
|
| Index. décimale : |
667.9 Revêtements et enduits |
| Résumé : |
Exterior surface coatings used in many applications can be exposed for long periods of time to cyclic exposure consisting of water submersion or local water surface puddling followed by water evaporation and solar exposure. Under such conditions, several macroscopic defects can appear including blistering, adhesion loss, soil pick-up, cracking, erosion, etc. However, quite often surface microscopic film defects can start long before these macroscopic defects are visibly evident. In this article, we show surface microscopic morphology changes to coatings cycled between water (submersion) and ultraviolet (UV) exposure where both polymer and formulation compositional factors were explored. Scanning electron microscopy (SEM) showed microscopic defects such as polymer-filler separation, filler removal, and degradation and crack formation appearance after short-term (one month) cyclic testing. The micrographs also revealed that the observed film defects were confined to the exposed surface and about a few filler particle diameters deep. |
| Note de contenu : |
- Table 1 : Flexible roof coating screening formulation |
| En ligne : |
https://drive.google.com/file/d/1RvyZQrUAznRtADhgH9ZZNGQocJdedeRU/view?usp=share [...] |
| Format de la ressource électronique : |
Pdf |
| Permalink : |
https://e-campus.itech.fr/pmb/opac_css/index.php?lvl=notice_display&id=34357 |
in COATINGS TECH > Vol. 17, N° 6 (06/2020) . - p. 28-35
Aller sur edunet
Accueil
Ajouter le résultat dans votre panier Affiner la rechercheMorphological changes in exterior surface coatings after exposure to cyclic water submersion and ultraviolet exposure in COATINGS TECH, Vol. 17, N° 6 (06/2020)