Fabrication of superhydrophobic cotton fabric treated with n-dodecyltrimethoxysilane/zirconium oxychloride for highly efficient oil/water separation / Weijing Zhao in JOURNAL OF COATINGS TECHNOLOGY AND RESEARCH, Vol. 17, N° 3 (05-06/2020)  

[article]  inJOURNAL OF COATINGS TECHNOLOGY AND RESEARCH > Vol. 17, N° 3 (05-06/2020) . - p. 657–668 Titre : Fabrication of superhydrophobic cotton fabric treated with n-dodecyltrimethoxysilane/zirconium oxychloride for highly efficient oil/water separation Type de document : texte imprimé Auteurs : Weijing Zhao, Auteur ; Xinyan Xiao, Auteur ; Guangming Pan, Auteur ; Zhihao Ye, Auteur Année de publication : 2020 Article en page(s) : p. 657–668 Note générale : Bibliogr. Langues : Américain (ame) Catégories : Caractérisation Coton Le coton est une fibre végétale qui entoure les graines des cotonniers "véritables"(Gossypium sp.), un arbuste de la famille des Malvacées. Cette fibre est généralement transformée en fil qui est tissé pour fabriquer des tissus. Le coton est la plus importante des fibres naturelles produites dans le monde. Depuis le XIXe siècle, il constitue, grâce aux progrès de l'industrialisation et de l'agronomie, la première fibre textile du monde (près de la moitié de la consommation mondiale de fibres textiles). Essais de résilience Fibres textiles -- Propriétés chimiques Fibres textiles -- Propriétés mécaniques Hydrophobie Hydroxyde de zirconium Séparation huile/eau Sol-gel, Procédé Textiles et tissus Index. décimale : 667.9 Revêtements et enduits Résumé : A simple sol–gel method was proposed to fabricate superhydrophobic cotton fabric (S-fabric) with a water contact angle of 155.6°. A co-condensation process between zirconium hydroxide (Zr(OH)4) and n-dodecyltrimethoxysilane under alkaline condition was presented. The functionalized Zr(OH)4 NPs with long-chain alkyl groups (–(CH2)11CH3) offered both hierarchical roughness and lower surface energy for S-fabric. The functional groups, surface morphology, element distribution, and surface roughness changes were examined by FTIR, SEM, EDS, and 3D optical profiler, respectively. And the results indicated that the cotton fabric was successfully modified. The obtained cotton fabric retained chemical stability after 72 h immersion in different extreme conditions, and mechanical durability after 200 cm of abrasion length. The S-fabric could be applied in the separation of oil–water mixture (n-hexane, n-heptane, n-dodecane, cyclohexane and kerosene) with the high efficiency (> 96%), and the efficiency remained stable after 50 separation cycles (n-dodecane and n-hexane). The facile preparation, chemical and mechanical stability, high separation efficiency, and good reusability of S-fabric indicated the potential practical application value in oil/water separation. Note de contenu : - EXPERIMENTAL SECTION : Materials - Fabrication of superhydrophobic cotton fabric - Characterizations - Chemical stability - Mechanical stability - Oil/water separation experiments - RESULTS AND DISCUSSION : Effect of the amount of ZrOCl2Æ8H2O and DTMSFTIR and XRD analysis - SEM and EDS analysis - Self-cleaning property - Chemical stability and mechanical stability - Oil/water separation DOI : https://doi.org/10.1007/s11998-019-00269-4 En ligne : https://link.springer.com/content/pdf/10.1007/s11998-019-00269-4.pdf Format de la ressource électronique : Pdf Permalink : https://e-campus.itech.fr/pmb/opac_css/index.php?lvl=notice_display&id=34097 [article]

Réservation

Réserver ce document

Exemplaires (1)

Code-barres	Cote	Support	Localisation	Section	Disponibilité
21734	-	Périodique	Bibliothèque principale	Documentaires	Disponible

---

1 (1 - 1 / 1)