| Titre : |
PEDOT-functionalized carbon nanotubes for anticorrosive reinforcement of epoxy coatings on sintered NdFeB magnets |
| Type de document : |
texte imprimé |
| Auteurs : |
Zihan Shen, Auteur ; Hongyi Yang, Auteur ; Pengjie Zhang, Auteur ; Jiewu Cui, Auteur ; Dongmei Wang, Auteur ; Wangqiang Shen, Auteur ; Guangqing Xu, Auteur ; Jun Lv, Auteur |
| Année de publication : |
2024 |
| Article en page(s) : |
p. 1677-1689 |
| Note générale : |
Bibliogr. |
| Langues : |
Américain (ame) |
| Catégories : |
Aimants
Anticorps
Anticorrosifs
Anticorrosion
Caractérisation
Charges (matériaux)
Electrophorèse
Epoxydes
Métaux -- Revêtements protecteurs
Nanotubes
Poly(3,4-éthylènedioxythiophène)
Revêtements organiques
|
| Index. décimale : |
667.9 Revêtements et enduits |
| Résumé : |
Solving the problems of interfacial compatibility and dispersibility between filler and epoxy resin (EP) can greatly improve the anticorrosion performances of epoxy coatings and expand their application field. In this work, carbon nanotubes (CNTs) were modified by poly(sodium 4-styrene sulfonate) and poly(3,4-ethylenedioxythiophene) to form PCNTs hybrids, and the cathodic electrophoretic deposition method was used to form composite epoxy coatings on the surface of sintered NdFeB magnets for enhancing the anticorrosion performance. The corrosion resistance of PCNTs was evaluated by electrochemical and static immersion corrosion tests. Results indicate that PCNTs hybrids possess better distribution and compatibility in epoxy resin than CNTs hybrids, resulting in the anticorrosion performances of higher density of composite epoxy coatings on NdFeB magnets. Optimized EP/PCNTs possess a much higher 0.01 Hz of 4.41 × 107 Ω·cm2 and a much lower Jcorr of 9.648 × 10− 10 A·cm− 2 than that of EP (1.34 × 104 Ω·cm2 and Jcorr 4.436 × 10− 6 A·cm− 2), demonstrating superior corrosion resistance. |
| Note de contenu : |
- EXPERIMENTAL
- Materials
- Synthesis of PCNTs hybrids
- Electrophoretic deposition of epoxy coatings
- Material characterizations and corrosion resistance tests
- RESULTS AND DISCUSSION :
- Characterization of PCNTs hybrids
- Characterization of composite epoxy coatings on NdFeB
- Anticorrosion performance of composite epoxy coatings on NdFeB
- Mechanism of corrosion protection |
| DOI : |
https://doi.org/10.1007/s11998-024-00924-5 |
| En ligne : |
https://drive.google.com/file/d/1AWy-nzZfXsLulQqFIYr7vf-w2VkpBo1P/view?usp=drive [...] |
| Format de la ressource électronique : |
Pdf |
| Permalink : |
https://e-campus.itech.fr/pmb/opac_css/index.php?lvl=notice_display&id=41519 |
in JOURNAL OF COATINGS TECHNOLOGY AND RESEARCH > Vol. 21, N° 5 (09/2024) . - p. 1677-1689
Aller sur edunet
Accueil
PEDOT-functionalized carbon nanotubes for anticorrosive reinforcement of epoxy coatings on sintered NdFeB magnets in JOURNAL OF COATINGS TECHNOLOGY AND RESEARCH, Vol. 21, N° 5 (09/2024)