Influence of PA6 as a charring agent on flame retardancy, thermal and mechanical properties of LGFR PP composites / M. Wang in INTERNATIONAL POLYMER PROCESSING, Vol. XXXIII, N° 4 (08/2018)  

[article]  inINTERNATIONAL POLYMER PROCESSING > Vol. XXXIII, N° 4 (08/2018) . - p. 535-542 Titre : Influence of PA6 as a charring agent on flame retardancy, thermal and mechanical properties of LGFR PP composites Type de document : texte imprimé Auteurs : M. Wang, Auteur ; L.-T. Li, Auteur ; L.-T. Li ; N. Wang ; Xiaolang Chen ; J.-B. Guo Année de publication : 2018 Article en page(s) : p. 535-542 Note générale : Bibliogr. Langues : Anglais (eng) Catégories : Calorimétrie Combustion Composites -- Propriétés thermiques Composites à fibres de verre Composites à fibres de verre -- Propriétés mécaniques Ignifugeants Composé chimique utilisé pour réduire l'inflammabilité. Il peut être incorporé au produit durant sa fabrication ou appliqué ultérieurement à sa surface. Microscopie électronique à balayage Polyamide 6 Pyrolyse La pyrolyse est la décomposition ou thermolyse d'un composé organique par la chaleur pour obtenir d'autres produits (gaz et matière) qu'il ne contenait pas. L'opération est réalisée en l'absence d'oxygène ou en atmosphère pauvre en oxygène pour éviter l'oxydation et la combustion (L’opération ne produit donc pas de flamme). Il s'agit du premier stade de transformation thermique après la déshydratation. Elle permet généralement d'obtenir un solide carboné, une huile et un gaz. Elle débute à un niveau de température relativement bas (à partir de 200 °C) et se poursuit jusqu'à 1 000 °C environ. Selon la température, la proportion des trois composés résultants est différente. Thermogravimétrie Index. décimale : 668.4 Plastiques, vinyles Résumé : In this work, the combustion, thermal, and mechanical performances of long-glass-fiber-reinforced polypropylene/intumescent flame retardant (LGFPP/IFR) composites with different contents of polyamide 6 (PA6) as a charring agent were investigated by limiting oxygen index (LOI), UL-94 test, cone calorimetry, thermal gravimetric analysis (TGA), scanning electron microscopy (SEM), and mechanical property test. The results showed that LGFPP/IFR/PA6 composites exhibited much better flame retardancy due to the dense char layer structure, as proved by SEM. When 15 wt% PA6 was added, the LGFPP/IFR composites had the best flame retardancy, and LOI increased by 55.1 %, and the UL-94 reached V-0 rating. The cone calorimeter tests indicated that PA6 could prevent the transmission of heat and the volatilization of flammable substances, thereby reducing the heat release of “second burning”. According to TGA analysis, the carbon layer began to form at a lower temperature due to the synergistic effect between IFR and PA6. Moreover, the calculation of apparent active energy (Ea) revealed that PA6 effectively increased the Ea values of the composites, resulting in a better thermal stability and flame retardancy. In addition, PA6 enhanced the mechanical properties of the composites effectively. Note de contenu : - EXPERIMENTAL : Raw materials - Experimental procedure - Measurements and charcterization - RESULTS AND DISCUSSION : Combustion behavior - Thermal degradation behavior - Static mechanical properties of flame retardant systems DOI : 10.3139/217.3549 En ligne : https://drive.google.com/file/d/1fYIpkkRs95YAUAKo2-j4bAKXFyq24EMm/view?usp=drive [...] Format de la ressource électronique : Pdf Permalink : https://e-campus.itech.fr/pmb/opac_css/index.php?lvl=notice_display&id=30893 [article]

Réservation

Réserver ce document

Exemplaires (1)

Code-barres	Cote	Support	Localisation	Section	Disponibilité
20077	-	Périodique	Bibliothèque principale	Documentaires	Disponible

---

1 (1 - 1 / 1)