Characterizing ultrasonic micro-molding process of polyetheretherketone (PEEK) |
| Type de document : |
texte imprimé |
| Auteurs : |
Tomasz Dorf, Auteur ; I. Ferrer, Auteur ; Joaquim Ciurana, Auteur |
| Année de publication : |
2018 |
| Article en page(s) : |
p. 442-452 |
| Note générale : |
Bibliogr. |
| Langues : |
Anglais (eng) |
| Catégories : |
Matières plastiques -- Moulage par injection assisté par ultrasons
Matières plastiques -- Moulage par micro-injection
Matières plastiques -- Propriétés mécaniques
Mesure
Polyéther éther cétone
|
| Index. décimale : |
668.4 Plastiques, vinyles |
| Résumé : |
Ultrasonic micro-molding technology can dispense, melt and inject as small an amount of polymer as is required for one cycle, an advantage which makes the process highly desirable for low-volume and customized production of micro parts made from sensitive and very expensive polymers, especially in the medical sector. In this study, the feasibility of processing the polyetheretherketone (PEEK) polymer was investigated. The experiments conducted determined the parameters of a process that would allow parts with specific mechanical properties to be produced and verified as not degraded. The development of the process used three amplitude values as well as varying plunger velocity and vibration times. The three amplitude values and four speed values were tested to determine appropriate parameters for the ultrasonic process. Completely filled samples without any visual signs of degradation were analysed using FTIR-ATR, crystallinity percentage and tensile strength tests. Results show that the amplitude parameter is an important factor in the ultrasonic process and the higher its value is, the better the mechanical properties of complete parts are. Moreover, the tensile strength value of the specimens fabricated by ultrasonic micro-molding is comparable to that of conventional injection molding technology. |
| Note de contenu : |
- EXPERIMENTAL SET-UP : Processing material - machine and equipment - Ultrasonic micro-molding process - Specimen manufacturing process - Part analysis and measurements
- RESULTS : Visual analysis of specimens - Degradation - Crystallinity - Tensile strength |
| DOI : |
10.3139/217.3428 |
| En ligne : |
https://drive.google.com/file/d/1sW6S0qJj6EtfYyAc-yxUudqb_iXOIRbG/view?usp=drive [...] |
| Format de la ressource électronique : |
Pdf |
| Permalink : |
https://e-campus.itech.fr/pmb/opac_css/index.php?lvl=notice_display&id=30883 |
in INTERNATIONAL POLYMER PROCESSING > Vol. XXXIII, N° 4 (08/2018) . - p. 442-452
Aller sur edunet
Accueil
Ajouter le résultat dans votre panier Affiner la rechercheCharacterizing ultrasonic micro-molding process of polyetheretherketone (PEEK) / Tomasz Dorf in INTERNATIONAL POLYMER PROCESSING, Vol. XXXIII, N° 4 (08/2018)