| Titre : |
Synthesis and performance investigation of carbon black hyperdispersant IMD |
| Type de document : |
texte imprimé |
| Auteurs : |
Shuangshuang Jiang, Auteur ; Jue Bai, Auteur ; Xiaogang Ying, Auteur ; Jianlin Han, Auteur ; Kai Zhu, Auteur ; Lianshan Mao, Auteur |
| Année de publication : |
2023 |
| Article en page(s) : |
p. 1529-1539 |
| Note générale : |
Bibliogr. |
| Langues : |
Américain (ame) |
| Catégories : |
Agents dispersants (chimie) -- Synthèse
Caractérisation
Dispersions et suspensions -- Stabilité
Formulation (Génie chimique)
Noir de carbone
Polyaddition
|
| Index. décimale : |
667.9 Revêtements et enduits |
| Résumé : |
An aqueous dispersion of carbon black is crucial in industrial coatings. In this manuscript, a hyperdispersant IBOMA-MPEGA-DMAM (IMD) has been synthesized using isobornyl methacrylate (IBOMA), polyethylene glycol monomethyl ether acrylate (MPEGA), and N, N-dimethyl acrylamide (DMAM) as monomers via a free radical polymerization method, which is used to improve the dispersibility of an aqueous dispersion system of carbon black. The molecular structure and performance stability of IMD were investigated through comprehensive characterizations of FTIR, GPC, particle size distribution and TEM. When the molar ratio of the monomers IBOMA:MEPGA:DMAM is 5.5:8.3:9.7, the obtained hyperdispersant shows good dispersibility. When the optimal dosage of dispersant IMD was 8%, the viscosity of carbon black slurry was as low as 18.6 mPa·s and the average particle size of carbon black was 275 nm. Furthermore, the stability of the prepared carbon black slurry was better than that of the two commercial dispersants. |
| Note de contenu : |
- EXPERIMENTAL : Materials - Synthesis of hyperdispersant IBOMA-MPEGA-DMAM - Preparation of CB pigment by dispersion system - Central composite design (CCD) - Characterization
- RESULTS AND DISCUSSION : CCD optimizes monomer ratio - FTIR analysis - GPC analysis - The viscosity of CB dispersion - The average particle size of the CB dispersion - TEM analysis - Stability of CB dispersions
- Table 1 : Formula of CB dispersion
- Table 2 : Factors and levels of central composite design
- Table 3 : Experimental results of central composite design
- Table 4 : Statistical analysis of the experimental results
- Table 5 : Prediction and experimental values of viscosity of CB slurry prepared with dispersant
- Table 6 : Relative molecular weight of IMD of superdispersant |
| DOI : |
https://doi.org/10.1007/s11998-023-00754-3 |
| En ligne : |
https://link.springer.com/content/pdf/10.1007/s11998-022-00754-3.pdf?pdf=button |
| Format de la ressource électronique : |
Pdf |
| Permalink : |
https://e-campus.itech.fr/pmb/opac_css/index.php?lvl=notice_display&id=39969 |
in JOURNAL OF COATINGS TECHNOLOGY AND RESEARCH > Vol. 20, N° 5 (09/2023) . - p. 1529-1539
Aller sur edunet
Accueil
Synthesis and performance investigation of carbon black hyperdispersant IMD in JOURNAL OF COATINGS TECHNOLOGY AND RESEARCH, Vol. 20, N° 5 (09/2023)