Investigation of the mechanical and thermal properties of LFR PA66 with graphene coating on fibre surface / S.-Y. Jin in INTERNATIONAL POLYMER PROCESSING, Vol. XXXIII, N° 2 (05/2018)  

[article]  inINTERNATIONAL POLYMER PROCESSING > Vol. XXXIII, N° 2 (05/2018) . - p. 286-291 Titre : Investigation of the mechanical and thermal properties of LFR PA66 with graphene coating on fibre surface Type de document : texte imprimé Auteurs : S.-Y. Jin, Auteur ; W.-W. Du, Auteur ; F. Benkhenafou, Auteur ; Lyes Douadji, Auteur Année de publication : 2018 Article en page(s) : p. 286-291 Note générale : Bibliogr. Langues : Anglais (eng) Catégories : Composites à fibres de verre Composites à fibres longues Enroulement Essais dynamiques Fibres de verre Graphène Le graphène est un cristal bidimensionnel (monoplan) de carbone dont l'empilement constitue le graphite. Il a été isolé en 2004 par Andre Geim, du département de physique de l'université de Manchester, qui a reçu pour cette découverte le prix Nobel de physique en 2010 avec Konstantin Novoselov. Il peut être produit de deux manières : par extraction mécanique du graphite (graphène exfolié) dont la technique a été mise au point en 2004, ou par chauffage d'un cristal de carbure de silicium, qui permet la libération des atomes de silicium (graphène epitaxié). Record en conduction thermique jusqu'à 5300 W.m-1.K-1. C'est aussi un matériaux conducteur. Matières plastiques -- Propriétés mécaniques Matières plastiques -- Propriétés thermiques Microscopie électronique à balayage Polyamide 66 Revêtements organiques Spectroscopie Raman Thermocinétique Index. décimale : 668.4 Plastiques, vinyles Résumé : An industrial fibreglass winding process is employed to apply graphene based sizing (0.2 wt% graphene concentration) on fibreglass surface. Both SEM and Raman spectroscopy characterization have proved that the coating of graphene on fibreglass surface is homogeneous and that the roughness of the fibreglass surface was improved. Long fiberglass-graphene reinforced PA66 pellets are successfully prepared through a pultrusion process. LGF-graphene-PA66 composites are produced following an injection molding process. Thermal conductivity was found to increase from 0.23 W/m · K−1 to 0.67 W/m · K−1 when compared with samples without graphene coating. The tensile strength of LGF-graphene-PA66 is 196 MPa while that of LGF-PA66 is 173 MPa. Tensile modulus is also found to increase to 13.5 GPa from 10.6 GPa after graphene coating. This new graphene coating process is a good method to produce high performance composites. Note de contenu : - EXPERIMENTAL METHODS : Materials - Model composites preparation - Scanning Electron Microscopy - Thermal conductivity of composites - Raman spectroscopy - Mechanical testing - RESULTS AND DISCUSSION : Scanning Electron Microscopy of fibres - Thermal conductivity of the composites - Raman spectroscopy of the fibres - Mechanical properties of the composites DOI : 10.3139/217.3604 En ligne : https://drive.google.com/file/d/1wHLpoZyflPUy__GytazGoptaU42ofX44/view?usp=drive [...] Format de la ressource électronique : Pdf Permalink : https://e-campus.itech.fr/pmb/opac_css/index.php?lvl=notice_display&id=30576 [article]

Réservation

Réserver ce document

Exemplaires (1)

Code-barres	Cote	Support	Localisation	Section	Disponibilité
19873	-	Périodique	Bibliothèque principale	Documentaires	Disponible

---

1 (1 - 1 / 1)