| Titre : |
Investigation of the adhesive strength in a combined compaction and back-injection process to produce back-injected self-reinforced composites (SRCs) |
| Type de document : |
texte imprimé |
| Auteurs : |
Fabian Jakob, Auteur ; Marcel Gothe, Auteur ; Fabian Gansiniec, Auteur ; Hans-Peter Heim, Auteur |
| Année de publication : |
2022 |
| Article en page(s) : |
p. 200-209 |
| Note générale : |
Bibliogr. |
| Langues : |
Anglais (eng) |
| Catégories : |
Adhésion
Compactage
Composites thermoplastiques auto-renforcés
Polypropylène
Rétro-injection
|
| Index. décimale : |
668.4 Plastiques, vinyles |
| Résumé : |
This publication investigates the adhesion between an injection molded component and a self-reinforced composite (SRC) produced in a combined compaction and back-injection process to produce back-injected self-reinforced composites. To study the influence of the process, the parameters barrel temperature, time of injection, and tool temperature were varied. In addition, samples were taken at different positions along the flow path. In light of the orthotropic material behavior of SRCs, investigations were conducted to see whether different loading cases lead to different mechanical behavior. Shear-off and pull-off tests revealed a different strength as a function of the loading type. In the shear-off tests, a mean strength of 11.37 MPa was recorded over the entire test series, while the measured mean strength in the pull-off tests is considerably lower, 4.04 MPa. The type of failure is determined with the aid of SEM images, and the influence of the microstructure of the thermoplastic fibre materials on the adhesion is set out. It is shown that, as of a sufficiently high level of adhesion, failure occurs within the fibres. |
| Note de contenu : |
- EXPERIMENTAL STUDIES : Materials - Processing - Preparation - Measuring
- RESULTS AND DISCUSSION : Shear-off tests - Pull-off tests - Microscopic observations
- Table 1 : Experimental setup for shear-off and pull-off tests |
| DOI : |
https://doi.org/10.1515/ipp-2022-4205 |
| En ligne : |
https://drive.google.com/file/d/13SX3M3UiFk-GU9y31gFAp-u48kddODJ5/view?usp=shari [...] |
| Format de la ressource électronique : |
Pdf |
| Permalink : |
https://e-campus.itech.fr/pmb/opac_css/index.php?lvl=notice_display&id=37625 |
in INTERNATIONAL POLYMER PROCESSING > Vol. 37, N° 2 (2022) . - p. 200-209
Aller sur edunet
Accueil
Investigation of the adhesive strength in a combined compaction and back-injection process to produce back-injected self-reinforced composites (SRCs) in INTERNATIONAL POLYMER PROCESSING, Vol. 37, N° 2 (2022)