Combinatorial approach to study the effect of acrylic polyol composition on the properties of crosslinked siloxane-polyurethane fouling-release coatings |
| Type de document : |
texte imprimé |
| Auteurs : |
Robert J. Pieper, Auteur ; Abdullah Ekin, Auteur ; Dean C. Webster, Auteur ; Franck Cassé, Auteur ; J. A. Callow, Auteur ; Maureen E. Callow, Auteur |
| Année de publication : |
2008 |
| Article en page(s) : |
p. 453-461 |
| Note générale : |
Bibliogr. |
| Langues : |
Américain (ame) |
| Catégories : |
Analyse thermique
Angle de contact
Chimie combinatoire
Chromatographie sur gel
Polyacryliques
Polyuréthanes
Résistance à la salissure
Revêtements -- Propriétés mécaniques:Peinture -- Propriétés mécaniques
Revêtements antisalissures:Peinture antisalissures
Salissures biologiques
Salissures marines
SiliconesLes silicones, ou polysiloxanes, sont des composés inorganiques formés d'une chaine silicium-oxygène (...-Si-O-Si-O-Si-O-...) sur laquelle des groupes se fixent, sur les atomes de silicium. Certains groupes organiques peuvent être utilisés pour relier entre elles plusieurs de ces chaines (...-Si-O-...). Le type le plus courant est le poly(diméthylsiloxane) linéaire ou PDMS. Le second groupe en importance de matériaux en silicone est celui des résines de silicone, formées par des oligosiloxanes ramifiés ou en forme de cage (wiki).
Transition vitreuse
|
| Index. décimale : |
667.9 Revêtements et enduits |
| Résumé : |
The effect of acrylic polyol composition on the properties of crosslinked siloxane-polyurethane coatings was explored. An acrylic polyol library was synthesized using batch solution polymerization and characterized using high-throughput gel permeation chromatography (Rapid-GPC) and differential scanning calorimetry (DSC). Siloxane-polyurethane coatings were prepared from 3-aminopropyl-terminated poly(dimethylsiloxane) (PDMS), the acrylic polyols and a polyisocyanate crosslinker. The siloxane-acrylicpolyurethane coatings were tested for mechanical and physical properties. The siloxane-polyurethane coatings had a systematic variation in glass transition temperature and had water contact angles ranging from 95° to 100°. Many of the coatings also showed a low-force of release in the pseudo-barnacle pull-off adhesion test. Performance testing of the fouling-release properties of the siloxane-polyurethane coatings on array panels with algae, namely the diatom Navicula and sporelings (young plants) of the green seaweed Ulva was also conducted. |
| DOI : |
10.1007/s11998-007-9032-1 |
| En ligne : |
https://link.springer.com/content/pdf/10.1007%2Fs11998-007-9032-1.pdf |
| Format de la ressource électronique : |
Pdf |
| Permalink : |
https://e-campus.itech.fr/pmb/opac_css/index.php?lvl=notice_display&id=3632 |
in JOURNAL OF COATINGS TECHNOLOGY AND RESEARCH > Vol. 4, N° 4 (12/2007) . - p. 453-461
Aller sur edunet
Accueil
Combinatorial approach to study the effect of acrylic polyol composition on the properties of crosslinked siloxane-polyurethane fouling-release coatings in JOURNAL OF COATINGS TECHNOLOGY AND RESEARCH, Vol. 4, N° 4 (12/2007)