Induction heating for cold weather preheating and post-curing of liquid epoxy coatings on gas pipeline girth welds / Bruce J. Wiskel in JOURNAL OF PROTECTIVE COATINGS & LININGS (JPCL), Vol. 33, N° 2 (02/2016)
[article]
Titre : Induction heating for cold weather preheating and post-curing of liquid epoxy coatings on gas pipeline girth welds Type de document : texte imprimé Auteurs : Bruce J. Wiskel, Auteur ; J. Peter Ault, Auteur Année de publication : 2016 Langues : Américain (ame) Catégories : Basses températures
Chauffage par induction
Climat
Epoxydes
Lignes de soudure
Revêtements protecteurs
Tuyaux de gazIndex. décimale : 667.9 Revêtements et enduits Résumé : Induction heating for cold weather pipeline girth welds - In 2013, Pacific Gas & Electric Company (PG&E) did not have a specific standard or guidance for selection, application and inspection of cold weather, field-applied coatings on transmission piping when the pipe surface temperatures went below 50 F (10 C). In November of that year, unusually cold weather hit northern California. Night temperatures were below freezing, which caused the pipe surface to be below the 50 F minimum necessary to cure the approved epoxy coatings.
At this time, the application procedure consisted of enclosing the work area and using space heaters to raise the ambient temperature sufficient to increase the pipe temperature. This approach was costly and cumbersome, and resulted in cure times of 6-to-10 hours or more. With these long cure times, construction crews could not quickly backfill the pipelines, and corresponding construction production rates were slow and costs high.Note de contenu : - COLD WEATHER COATING CHALLENGES
- LOW-TEMPERATURE COATING
- INDUCTION HEATING : Laboratory demonstrations - Field demonstrations
- AN ALTERNATIVE PIPE-HEATING PRACTICEPermalink : https://e-campus.itech.fr/pmb/opac_css/index.php?lvl=notice_display&id=25629
in JOURNAL OF PROTECTIVE COATINGS & LININGS (JPCL) > Vol. 33, N° 2 (02/2016)[article]Réservation
Réserver ce document
Exemplaires (1)
Code-barres Cote Support Localisation Section Disponibilité 17889 - Périodique Bibliothèque principale Documentaires Disponible Preventing crevice corrosion in new and existing steel structures / Eric Shoyer in JOURNAL OF PROTECTIVE COATINGS & LININGS (JPCL), Vol. 35, N° 1 (01/2018)
![]()
[article]
Titre : Preventing crevice corrosion in new and existing steel structures Type de document : texte imprimé Auteurs : Eric Shoyer, Auteur ; J. Peter Ault, Auteur ; Peter McDonagh, Auteur ; Brian Prazenka, Auteur Année de publication : 2018 Article en page(s) : p. 20-32 Langues : Américain (ame) Catégories : Acier L'acier est un alliage métallique utilisé dans les domaines de la construction métallique et de la construction mécanique.
L'acier est constitué d'au moins deux éléments, le fer, très majoritaire, et le carbone, dans des proportions comprises entre 0,02 % et 2 % en masse1.
C'est essentiellement la teneur en carbone qui confère à l'alliage les propriétés du métal qu'on appelle "acier". Il existe d’autres métaux à base de fer qui ne sont pas des aciers comme les fontes et les ferronickels par exemple.
Anticorrosifs
Anticorrosion
Corrosion
Métaux -- Revêtements protecteursIndex. décimale : 667.9 Revêtements et enduits Résumé : Bolted joints in steel structures contain multiple crevices between the bolted members and the fasteners that are typically more susceptible to corrosion than flat surfaces, and difficult to properly coat. This article will evaluate the effectiveness of various coating practices at mitigating corrosion around these joints. Note de contenu : - THE TEST APPROACH : Panel design - Weathered steel - New steel - Coating application - Caulking methods - Corrosion testing
- RESULTS : Crevice corrosion - Bolt corrosion - Disassembly - Pit depth
- TABLES : 1. Study Test Matrix - 2. Crevice Corrosion Inspection at 120 Cycles of GMW 14872 - 3. Corrosion of Black-Oxide Bolts on Panels - 4. Percentage of Galvanized Bolts Displaying Corrosion per Panel - 2. Crevice Corrosion Inspection at 120 Cycles of GMW 14872 - 3. Corrosion of Black-Oxide Bolts on Panels - 4. Percentage of Galvanized Bolts Displaying Corrosion per Panel
- FIGURES : 1. Front and back of panels after weathering - 2. Surface preparation after weathering (SSPC-SP 10 left, SSPC-SP 11 right) - 3. New steel panels (assembled prior to blast, left ; post-SSPC-SP 10 blast, center ; and SSPC-SP 10 blast and primed, then assembled right) - 4. Caulking scenarios, side view (top method, top left ; 3/4 method, top right ; and full method, bottom) - 5. One cycle of GMW 14872 - 6. New steel primed after assembly - 7. New steel primed before assembly - 8. Weathered steel, SSPC-SP 10 remediation - 9. Weathered steel, SSPC-SP 11 remediation - 10. Panels disassembled after application - 11. Minimum, average and maximum pits measured on the crevice face of the angle for panels representing new steel coating systems - 12. Minimum, average and maximum pits measured on the crevice face of the angle for panels representing weathered steel coating systems - 13. L channel before and after glass-bead blastingEn ligne : http://www.paintsquare.com/archive/?fuseaction=view&articleid=6237 Format de la ressource électronique : Web Permalink : https://e-campus.itech.fr/pmb/opac_css/index.php?lvl=notice_display&id=30365
in JOURNAL OF PROTECTIVE COATINGS & LININGS (JPCL) > Vol. 35, N° 1 (01/2018) . - p. 20-32[article]Réservation
Réserver ce document
Exemplaires (1)
Code-barres Cote Support Localisation Section Disponibilité 19617 - Périodique Bibliothèque principale Documentaires Disponible Standard used for partial coating removal during maintenance painting / J. Peter Ault in JOURNAL OF PROTECTIVE COATINGS & LININGS (JPCL), Vol. 34, N° 7 (07/2017)
![]()
[article]
Titre : Standard used for partial coating removal during maintenance painting Type de document : texte imprimé Auteurs : J. Peter Ault, Auteur ; Eric Shoyer, Auteur Année de publication : 2017 Article en page(s) : p. 36-44 Note générale : Bibliogr. Langues : Américain (ame) Catégories : Abrasion par jet d'eau
Coût -- Contrôle
Durée de vie (Ingénierie)
Surfaces -- Nettoyage
Traîtements de surface
Traîtements de surface -- NormesIndex. décimale : 667.9 Revêtements et enduits Résumé : Partial surface preparation is a cost-saving concept with merit and demonstrated success in low-risk applications. This article details the challenges one must overcome prior to adopting partial surface preparation for high-risk applications with long desired service life. Note de contenu : - Standards for partial coating removal
- Technical challenges associated with partial coating removal
- Costs savings
- Expected service life
- Table 1. Relevant abrasive blasting surface preparation standards
- Table 2. Relevant waterjetting surface preparation standardsEn ligne : http://www.paintsquare.com/archive/?fuseaction=view&articleid=6090 Format de la ressource électronique : Web Permalink : https://e-campus.itech.fr/pmb/opac_css/index.php?lvl=notice_display&id=29486
in JOURNAL OF PROTECTIVE COATINGS & LININGS (JPCL) > Vol. 34, N° 7 (07/2017) . - p. 36-44[article]Réservation
Réserver ce document