Investigations on blending and foaming behavior of styrehe-ethylene-butylene-styrene/polystyrene blends |
| Type de document : |
texte imprimé |
| Auteurs : |
R. Banerjee, Auteur ; S. S. Ray, Auteur ; Anuk K. Ghosh, Auteur |
| Année de publication : |
2017 |
| Article en page(s) : |
p. 434-445 |
| Note générale : |
Bibliogr. |
| Langues : |
Anglais (eng) |
| Catégories : |
Alliages polymères
Alliages polymères -- propriétés mécaniques
Analyse mécanique dynamique
Copolymère styrène-éthylène-butadiène
Essais dynamiques
Matières plastiques -- Extrusion
Microscopie électronique à balayage
Mousses plastiques
Polystyrène
Rhéologie
Traction (mécanique)
|
| Index. décimale : |
668.4 Plastiques, vinyles |
| Résumé : |
The interplay of screw speed and residence time during polymer blend extrusion profoundly influences blend properties. Herein, blends of styrene-ethylene-butylene-styrene (SEBS) and polystyrene (PS) containing 30% by weight PS were prepared at a constant feed rate but different screw speeds (50, 100, 200 and 300 min?1). The blend produced at 100 min?1 (B100) possessed a finer morphology, better mechanical and rheological properties, attributed to suitability of residence time and viscosity ratio. When batch foamed with carbon dioxide at 110°C and 100°C, all blends produced stable foams. B100 foams exhibited higher volume expansion ratio (VE) due to higher complex viscosity and storage modulus. When foaming was conducted at 35°C, all foams shrank. B100 foams possessed higher cell density, lower VE and showed faster shrinkage due to increased nucleation and hindered expansion by the finely dispersed stiff PS aggregates during selective foaming of the elastomeric phase. |
| Note de contenu : |
- EXPERIMENTAL : Raw materials - Melt state rheological studies - Blend sample preparation - Tensile test - DMA studies - Batch foaming - Shrinkage of foams with time
- RESULTS AND DISCUSSION : Melt state rheological studies of SEBS and PS - Residence time determination - SEM studies of the blends - Tensile test - DMA studies - Shrinkage of foams with time - SEM studies of foams |
| DOI : |
10.3139/217.3362 |
| En ligne : |
https://drive.google.com/file/d/1mpJdRLK39C2M4O2OBrUxvCDBUfkki3MO/view?usp=drive [...] |
| Format de la ressource électronique : |
Pdf |
| Permalink : |
https://e-campus.itech.fr/pmb/opac_css/index.php?lvl=notice_display&id=28900 |
in INTERNATIONAL POLYMER PROCESSING > Vol. XXXII, N° 4 (08/2017) . - p. 434-445
Aller sur edunet
Accueil
Investigations on blending and foaming behavior of styrehe-ethylene-butylene-styrene/polystyrene blends in INTERNATIONAL POLYMER PROCESSING, Vol. XXXII, N° 4 (08/2017)