Influence of nano-boron nitride on anti-aging property of waterborne fire-resistive coatings / Ying Dong in JOURNAL OF COATINGS TECHNOLOGY AND RESEARCH, Vol. 11, N° 5 (09/2014)  

[article]  inJOURNAL OF COATINGS TECHNOLOGY AND RESEARCH > Vol. 11, N° 5 (09/2014) . - p. 805-815 Titre : Influence of nano-boron nitride on anti-aging property of waterborne fire-resistive coatings Type de document : texte imprimé Auteurs : Ying Dong, Auteur ; Guojian Wang, Auteur ; Qin Su, Auteur Année de publication : 2014 Article en page(s) : p. 805-815 Note générale : Bibliogr. Langues : Américain (ame) Catégories : Essais accélérés (technologie) Ignifugeants Composé chimique utilisé pour réduire l'inflammabilité. Il peut être incorporé au produit durant sa fabrication ou appliqué ultérieurement à sa surface. Intumescence (chimie) Nitrure de bore Le nitrure de bore est un composé chimique du bore et de l'azote, de formule chimique brute BN (nombre égal d'atomes de chaque élément). Le nitrure de bore est isoélectronique avec le carbone et, comme ce dernier, existe sous plusieurs formes polymorphiques, dont l'une est analogue au diamant et l'autre au graphite. La forme diamant est l'un des matériaux les plus durs connus et la forme graphite est un lubrifiant apprécié. De plus, ces deux polymorphes possèdent des propriétés d'absorption radar. Résistance au vieillissement Résistance thermique Revêtements en phase aqueuse:Peinture en phase aqueuse Revêtements multicouches Stabilité thermique Index. décimale : 667.9 Revêtements et enduits Résumé : The influence of nano-boron nitride (BN) with a multilayered structure on the anti-aging property of fire-resistive coatings was studied. After accelerated weathering for 20 days, the thermal stabilities and fire protection of the coating without nano-BN were significantly decreased, but the coating modified by nano-BN still maintained excellent intumescent effect and fire protection. The results indicated that nano-BN could improve the anti-aging property of the coatings remarkably. FTIR and XPS characterizations suggested that nano-BN with a multilayered structure could prevent the migration behavior of the hydrophilic fire-retardant additives and keep the fixed ratio of those additives in the coating. TGA results demonstrated that nano-BN could effectively enhance the thermal stabilities of the aged coatings and improve the anti-oxidation property of the char layers formed by the coatings. XRD and EDS results proved that the anti-oxidation of the aged coatings under high temperature could be enhanced effectively after adding nano-BN. SEM observations illustrated that nano-BN addition was beneficial to the improvement of the foam structure of the aged coating. Note de contenu : - EXPERIMENTAL : 1. Materials - 2. Sample preparation - 3. Accelerated aging tests - 4. Fire protection test - 5. Measurements and characterizations - RESULTS AND DISCUSSION : 1. Influence of nano-BN on fire protection of aged coatings - 2. Influence of nano-BN on thermal stabilities of aged coatings - 3. Influence of nano-BN on chemical structure of aged coatings - 4. Influence of nano-BN on structure and elemental compositions of the char layers - 5. Morphological structure and elemental composition of the char layer DOI : 10.1007/s11998-013-9538-7 En ligne : https://link.springer.com/content/pdf/10.1007%2Fs11998-013-9538-7.pdf Format de la ressource électronique : Pdf Permalink : https://e-campus.itech.fr/pmb/opac_css/index.php?lvl=notice_display&id=22063 [article]

Réservation

Réserver ce document

Exemplaires (1)

Code-barres	Cote	Support	Localisation	Section	Disponibilité
16538	-	Périodique	Bibliothèque principale	Documentaires	Disponible

---

1 (1 - 1 / 1)