Flame retarded PE with MH/ATH/microencapsulated red phosphorous and its toughening by polymeric compatibilizers / Xiaodong Hong in INTERNATIONAL POLYMER PROCESSING, Vol. XXIX, N° 4 (08/2014)  

[article]  inINTERNATIONAL POLYMER PROCESSING > Vol. XXIX, N° 4 (08/2014) . - p. 447-453 Titre : Flame retarded PE with MH/ATH/microencapsulated red phosphorous and its toughening by polymeric compatibilizers Type de document : texte imprimé Auteurs : Xiaodong Hong, Auteur ; B. Liang, Auteur ; D.-X. Yang, Auteur Année de publication : 2014 Article en page(s) : p. 447-453 Note générale : Bibliogr. Langues : Anglais (eng) Catégories : Composés inorganiques -- Synthèse Composites -- Propriétés mécaniques Encapsulation Ethylène-propylène-diène monomère Hydroxyde d'aluminium Hydroxyde de magnésium L'hydroxyde de magnésium est un composé inorganique de formule Mg(OH)2. Ce sel se présente sous la forme d'une poudre pratiquement insoluble dans l'eau. Le « lait de magnésie » est une solution saturée d'hydroxyde de magnésium, d'aspect laiteux. Sa forme minérale naturelle est connue sous le nom de brucite. L'hydroxyde de magnésium est utilisé en thérapeutique comme antiacide (pour calmer les brûlures d'estomac) et comme laxatif. Hydroxydes métalliques Ignifugeants Composé chimique utilisé pour réduire l'inflammabilité. Il peut être incorporé au produit durant sa fabrication ou appliqué ultérieurement à sa surface. Phosphore Polyéthylène Polyéthylène glycol Polymérisation Index. décimale : 668.4 Plastiques, vinyles Résumé : Non-halogen flame retarded polyethylene (PE) can be prepared by filling metallic hydroxides magnesium hydroxide (MH) or aluminium hydroxide (ATH), the mechanical properties of polymer composites will decline greatly when filling much more inorganic particles. Selecting microencapsulating particles, suitable synergistic agents or compatibilizers are good methods for improving the combination performance of composites. In this study, microencapsulated red phosphorous (MRP) was synthesized by using melamine-formaldehyde resin through in-situ polymerization, and used as a synergistic agent of MH and ATH, and the best proportion of three flame retardants was studied in detail. Results showed that flame retarded PE had a better combination performance when filling with 45 wt% compound flame retardants of MRP, MH and ATH under the weight ratio of 46/46/8. In order to improve the mechanical performance of composite, two polymeric compatibilizers POE-g-MAH and EPDM-g-MAH were selected to toughen the flame retarded PE composite. Results showed the flame resistance and mechanical properties of composites improved greatly with an increase of compatibilizer content, under the same condition, POE-g-MAH has a better contribution on the flame resistance and EPDM-g-MAH has a better toughening effect. The best flame retarded PE composite can be obtained by filling with 45 wt% compound flame retardants and 10 wt% EPDM-g-MAH. Note de contenu : - Characterization of MRP - Synergy effect of MRP - Toughening of non-halogen retarded PE - Microstructure analysis on the surface of fracture DOI : 10.3139/217.2831 En ligne : https://drive.google.com/file/d/1YetbZf7TEhedI3UdJ4fr3-OcEKFZF_SR/view?usp=drive [...] Format de la ressource électronique : Pdf Permalink : https://e-campus.itech.fr/pmb/opac_css/index.php?lvl=notice_display&id=21823 [article]

Réservation

Réserver ce document

Exemplaires (1)

Code-barres	Cote	Support	Localisation	Section	Disponibilité
16454	-	Périodique	Bibliothèque principale	Documentaires	Disponible

---

1 (1 - 1 / 1)